将TEOS,镁铝硝酸盐以及一定量的尿素溶于乙醇-水溶液。100℃水浴加热形成凝胶。凝胶干燥后,高温煅烧可得到一种镁铝硅复合氧化物粉体。对在不同温度下煅烧的粉体和1350℃烧结的样品进行X射线衍射分析,发现在煅烧过程中,基体形态经历了从无定形态向晶态α-堇青石的转化过程,并伴随有μ-堇青石相,镁铝尖晶石相和β-石英固溶体的出现和消失。1350℃烧结的样品全部为α-堇青石相,烧结致密度最高达99.5％。以扫描电镜观察该样品的表面形貌,可看出其晶粒呈薄片状。并对纯堇青石的致密化烧结过程进行了探讨。
The TEOS, stoichiometric magnesium nitrate and aluminum nitrate, and some carbamide were dissolved in the
solution of CH3CH2OH-H2O. The solution was heated at 100℃ and then transformed into gelatinate. The dried gelatinate calcined at high
temperature and a compound of MgO, Al2O3 and SiO2 could be obtained. The powder calcined at different temperatures and the sample sintered at
1350℃ for 2h were examined by using XRD. The X-Ray diffraction studies indicate that the forms of the matrix when heat-treated come through
a progress from amorphous compound to α-cordierite, with the appearance and disappearance of μ-cordierite, spinel and β-SiO2. The whole
sample sintered at 1350℃ is made of α-cordierite. The highest density of the samples is 99.5%. The SEM micrograph of the sample
shows that the grain is flake. The densification process of pure cordierite ceramics was investigated.
参考文献
| [1] | Haase W, Sedda L. Ceram．Forum. Int., 1999, 76 (7): 9--14. [2] Gonzalez-Velasco J R, Gutierrez-Ortiz M A, Ferret R, et al. J. Mater. Sci., 1999, 34 (9): 1999--2002. [3] SEN M, YANG J, JOSE M F F. J. Mater Lett., 2001, 47 (4-5): 205--211. [4] Yi Hu, Tsai H T. J. Non-Crystalline. Solids., 2001, 286: 51--57. [5] Wu Jenn-ming, Huang Hong-lin. J. Mater. Res., 2000, 15 (1): 222--227. [6] Shyu Jiin-Jyh, Wang Jui-Kai. J. Mater. Res., 2000, 15 (8): 1759--1765. [7] Cai Shu, Xu Mingxia, Zhou Cailou, et al. Mater. Res. Bull., 2002, 37: 133--134. [8] PAL D, CHAKRABORTY A K, SUCHITRA S. J. Mater. Sci., 1996, 31: 3955--4005. [9] Oh J R, Imai H, Hirashima H. J. Ceram. Soc. Jpn., 1997, 105 (1): 43--47. [10] 谭斌源, 刘继泉, 潘伟超. 青岛化工学院学报, 1998, 19 (2): 194--195. [11] LIU Chao-feng, et al. Journal of Inorganic Materials., 1999, 14 (3): 391--395. [12] LIU Jian, et al. Journal of Inorganic Materials., 1993, 8 (4): 423--427. [13] LIU Jian, Chen Jijian. Journal of East China Institute of Chemical Technology., 1992, 18: 28--32. [14] 高瑞平, 李晓光. 先进陶瓷物理与化学原理及技术, 第一版. 北京: 科学出版社, 2001. 297--337. [15] Zheng J, Reed J S. J. Am. Ceram. Soc., 1989, 72 (5): 810--817. [16] JIN Xi-Hai, et al. Journal of Inorganic Materials., 2001, 16 (3): 555--558. [17] Wu Jenn-Ming, Huang Hong-Li. J. Mater. Res., 2000, 15 (1): 222--227. |