采用阴极电弧离子镀技术在1Cr13不锈钢表面制备了ZrN梯度层和Zr/ZrN多层膜,并用电化学腐蚀方法和中性盐雾法检测了1Cr13基体、ZrN梯度层和Zr/ZrN多层膜的耐腐蚀性能.结果表明:Zr/ZrN多层膜和ZrN梯度层均能提高1Cr13基体的抗腐蚀能力,而Zr/ZrN多层膜的效果更明显:镀层的内部缺陷(如微孔)和液滴导致薄膜发生孔蚀、隙缝腐蚀和电偶腐蚀;镀层保护的实质是物理屏障作用,细化晶粒、减少膜层中的液滴及针孔等缺陷能显著提高薄膜的抗腐蚀性能.
参考文献
| [1] | Marco J.F.;Gancedo J.R.;Hanzel D.;Agudelo A.C. .Corrosion resistance of single TiN layers, Ti/TiN bilayers and Ti/TiN/Ti/TiN multilayers on iron under a salt fog spray (Prohesion) test: An evaluation by XPS[J].Surface and Interface Analysis: SIA: An International Journal Devoted to the Development and Application of Techniques for the Analysis of Surfaces, Interfaces and Thin Films,1999(2):71-75. |
| [2] | B. F. Chen;W. L. Pan;G. P. Yu;J. Hwang;J. H. Huang .On the corrosion behavior of TiN-coated AISI D2 steel[J].Surface & Coatings Technology,1999(1):16-21. |
| [3] | BIN-SUDIN M;LEYLAND A;JAMESA S et al.Substrate surface finish effects in duplex coatings of PAPVD TIN and CrN with electroless nickel-phosphorus intexlayers[J].Surface and Coatings Technology,1996,81(2/3):215-224. |
| [4] | 鲜晓斌,王庆富,刘柯钊,刘清和.阴极电弧离子沉积TiN/Ti镀层腐蚀特性[J].稀有金属材料与工程,2005(11):1774-1777. |
| [5] | 刘浩宇.碳钢表面陶瓷化耐腐蚀性能的研究（续）[J].设备管理与维修,2005(11):12-14. |
| [6] | 史新伟,李杏瑞,邱万起,刘正义.电弧离子镀TiN及其复合膜的腐蚀机理探讨[J].真空科学与技术学报,2006(04):330-334. |
| [7] | 李瑛,屈力,王福会,邵忠宝.TiN涂层电化学腐蚀行为研究Ⅰ.TiN涂层的保护性能与失效机制[J].中国腐蚀与防护学报,2003(02):65-69. |
| [8] | 梁成浩.离子镀TiN膜对不锈钢在海水中缝隙腐蚀行为的影响[J].腐蚀科学与防护技术,1995(02):167. |
| [9] | 李成明,孙晓军,张增毅,唐伟忠,吕反修.ZrN及其多层膜的性质和耐腐蚀性能[J].材料热处理学报,2003(04):55-58. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%