研究不同酸处理对碳纳米管的微观结构和形貌的影响,采用SEM和XRD对其进行表征.SEM观测表明经过酸处理后的碳纳米管杂质明显减少;1∶1的浓H2SO4、浓HNO3混酸处理后,碳纳米管长径比降低,不易发生团聚,分散性提高,并保持了其优异的性能;通过比较得出超声处理比高温回流处理所得碳纳米管表面质量更优;XRD分析表明3:1的浓H2SO4、浓HNO3混酸氧化刻蚀能力较强,对碳纳米管的晶体结构破坏严重.
参考文献
| [1] | Iijima S;Ichihashi T .Single-shell carbon nanotubes of 1-nm diameter[J].Nature,1993,363(6430):603. |
| [2] | Rong Zhong;Hongtao Cong;Pengxiang Hou .Fabrication of nano-Al based composites reinforced by single-walled carbon nanotubes[J].Carbon: An International Journal Sponsored by the American Carbon Society,2003(4):848-851. |
| [3] | 黎沙泥,许向彬,李忠明,杨鸣波.碳纳米管的表面修饰及其在聚合物中的应用[J].工程塑料应用,2004(10):70-72. |
| [4] | 晋卫军,孙旭峰,王煜.碳纳米管溶解性及其化学修饰[J].新型炭材料,2004(04):312-318. |
| [5] | 曹茂盛,刘海涛,李辰砂,陈玉金,马文有.碳纳米管表面处理技术的研究[J].中国表面工程,2002(04):32-36. |
| [6] | 江琳沁,高濂.化学处理对碳纳米管分散性能的影响[J].无机材料学报,2003(05):1135-1138. |
| [7] | Shaffer MSP.;Windle AH.;Fan X. .Dispersion and packing of carbon nanotubes[J].Carbon: An International Journal Sponsored by the American Carbon Society,1998(11):1603-1612. |
| [8] | 贾志杰 .碳纳米管/高分子复合材料的研究[D].清华大学,1999. |
| [9] | 曹茂盛;曹传宝;徐甲强.纳米材料学[M].哈尔滨:哈尔滨工 程大学出版社,2002 |
| [10] | Satio T et al.Chemical treatment and modification of multiwalled carbon nanotubes[J].Physica B,2002,323(01):280. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%