制备了以ZnO-B2O3-P2O5为基体,外加金属氧化物(Fe2O3, MnO2, CuO和 TiO2)的玻璃试样,研究了金属氧化物对玻璃膨胀系数、密度、玻璃转变温度、软化点温度、化学稳定性、电阻率的影响.实验结果表明外加金属氧化物Fe2O3对提高玻璃的化学稳定性最为有效,MnO2不仅在提高磷酸盐玻璃的化学稳定性方面效果优异,同时在降低玻璃的封接温度方面效果明显,CuO、TiO2对封接性能的影响介于上述二者之间.通过扫描电镜、红外光谱分析了玻璃结构的变化.
参考文献
| [1] | 郭宏伟,刘新年,高档妮.低熔封接玻璃无铅化的研究现状及发展趋势[J].中国玻璃,2005(03):3-6. |
| [2] | European Commission .Draft proposal for a European parliament and council directive on waste electric and electronic equipment[R].Brussels,Belgium,2000. |
| [3] | 祝大同.新世纪：走向绿色化的电子产品--"EGG'2000"国际会议侧记[J].世界电子元器件,2001(06):70-74. |
| [4] | Lisitsyna E A .Production and structure of the glasses 0.4Zn(PO3)2·(0.6-x) Al(PO3)3·x(PO3)3[J].Journal of Physics and Chemistry of Glasses,1998,14(04):333-336. |
| [5] | Takebe H;Baba Y;Kuwabara M .Dissolution behavior of ZnO-P2O5 glasses in water[J].Journal of Non-Crystalline Solids: A Journal Devoted to Oxide, Halide, Chalcogenide and Metallic Glasses, Amorphous Semiconductors, Non-Crystalline Films, Glass-Ceramics and Glassy Composites,2006(28/29):3088-3094. |
| [6] | L. Koudelka;P. Mosner .Borophosphate glasses of the ZnO-B2O3-P2O5 system[J].Materials Letters,2000(3):194-199. |
| [7] | Hirose J .Glass composition and glass forming material comprising said composition[P].US 20030125185,2003-08-27. |
| [8] | 李胜春,陈培.B2O3对Zn-B-P低熔电子玻璃结构和性能的影响[J].电子元件与材料,2007(09):65-67. |
| [9] | 李胜春;陈培 .一种电子浆料无铅低熔玻璃及制备方法[P].CN 101058478,2007-3-30. |
| [10] | Mogus-Milankovic A;Gajovic A;Santic A et al.Structure of sodium phosphate glasses containing Al2O3 and/or Fe2O3[J].Part I Journal of Non-Crystalline Solids,2001,289:204-213. |
| [11] | Santis A;Mogus-Milankovic A;Furic K et al.Structural properties of Cr2O3-Fe2O3-P2O5 glasses[J].Part I Journal of Non-Crystalline Solids,2007,353:1070-1077. |
| [12] | 刘秋霞,闫玉华.B2O3对磷酸盐生物玻璃水解性的影响[J].武汉工业大学学报,1998(03):34-36. |
| [13] | 王国明,杨国昱.硼-锗骨架无机微孔材料研究进展[J].无机化学学报,2006(08):1359-1370. |
| [14] | Boonchom B;Youngme S;Maensiri S et al.Nanocrystalline serrabrancaite[J].Journal of Alloys and Compounds,2008,454:78-82. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%