The influence of an alternative magnetic field on the diffusion of Al and Mg in Al-Mg diffusion couple is studied. The diffusion zone is composed of two intermediate phases, namelyβ and γ phase. Thickness of each intermediate phase is examined. The results show that the alternative magnetic field increases the thicknesses ofβ and γ phase zone and the layer growth ofβ and γ phase obeys the parabolic rate law. The growth rate of theβ and γ phase are increased with the application of the alternative magnetic field. This change is manifested through a change in the frequency factor ko and not through a change in the activation energy Q. The frequency factor ko for intermediate phase growth with an alternative magnetic field is 39.95 cm2/s for γ phase and 2.84×10-4 cm2/s for β phase compared with those without the magnetic field is 22.4 cm2/s for γ phase and 1.53×10-4 cm2/s forβ phase.
参考文献
| [1] | M Furui;Y Kojima;M Matsuo .[J].ISM International,1993,33(03):400. |
| [2] | M.Shimotomai;K.Maruta .[J].Scripta Materialia,2000,42:499. |
| [3] | S Kawai .[J].Materials Transactions,2001,42:275. |
| [4] | ShigeoAsai .[J].ISIJ International,1989,29(12):981. |
| [5] | J Zhang;J Z Cui;G M Lu .[J].Materials Letters,2003,57:1707. |
| [6] | ChunyanAN .PhD Thesis[D].Northeastern UniversityShenyang,2002. |
| [7] | M Hansen;K.Auderko.Constitution of Binary Alloys[M].McGraw Hill, New York,1958:105. |
| [8] | ShiminHAO .[J].mater Metall,2002,1(03):166. |
| [9] | S Samson .[J].Acta Crystallographica,1965,19:401. |
| [10] | F Laves;K Moeller .[J].Zeitschrift Fur Metallkunde,1938,30:232. |
| [11] | E Fromm .[J].Zeitschrift fur Metallkunde,1966,57:60. |
| [12] | C Wagner .[J].Acta Materialia,1969,17:99. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%