采用溶液共混及原位复合法制备多壁碳纳米管/杂萘联苯聚醚砜酮复合材料.通过扫描电镜观察材料的形貌,并对材料性能进行研究.对比两种方法,结果表明通过原位复合法制备,碳管在基体中有较好的分散和界面结合,其力学性能和导电性优于溶液共混法制备的复合材料.当碳管含量为3%(质量分数)时,原位复合材料的拉伸模量和强度分别为2.4GPa和107.6MPa,其体积电阻率达到1.0×106 Ω·cm,5%热失重温度提高了20℃.
参考文献
[1] | Salvetat J.-P.;Thomson N.H.;Kulik A.J.;Forro L.;Benoit W.;Zuppiroli L.;Bonard J.-M. .Mechanical properties of carbon nanotubes[J].Applied physics, A. Materials science & processing,1999(3):255-260. |
[2] | Demczyk BG.;Wang YM.;Cumings J.;Hetman M.;Han W.;Zettl A.;Ritchie RO. .Direct mechanical measurement of the tensile strength and elastic modulus of multiwalled carbon nanotubes[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2002(1/2):173-178. |
[3] | 车如心,高宏,赵宏滨.溶胶-凝胶法制备纳米复合永磁材料及其磁性[J].功能材料,2006(01):146-149. |
[4] | Iijima S .[J].Nature,1991,354:56-58. |
[5] | Fisher F T;Bradshaw B D;Brinson L C .[J].Applied Physics Letters,2002,80(24):4647-4649. |
[6] | Kim Y J;Shin T S;Choi H D .[J].Carbon,2005,43:23-30. |
[7] | 方芳,张清华,常振军,陈大俊.碳纳米管/聚苯乙烯复合材料的制备及导电性能研究[J].功能材料,2007(04):659-661. |
[8] | 蹇锡高,陈平,廖功雄,朱秀玲,张守海,王锦艳.含二氮杂荼酮结构新型聚芳醚系列高性能聚合物的合成与性能[J].高分子学报,2003(04):469-475. |
[9] | Meng YZ.;Jian XG.;Tjong SC.;Hay AS. .SYNTHESIS OF NOVEL POLY(PHTHALAZINONE ETHER SULFONE KETONE)S AND IMPROVEMENT OF THEIR MELT FLOW PROPERTIES[J].Journal of Applied Polymer Science,1997(8):1425-1432. |
[10] | Lai M F;Li J;Yang J .[J].Polymer International,2004,53:1479-1484. |
[11] | Shaffer MSP.;Windle AH. .Fabrication and characterization of carbon nanotube/poly(vinyl alcohol) composites[J].Advanced Materials,1999(11):937-941. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%