利用神经网络建模研究强化杨木单板复合材料的制备工艺.研究中利用三种乙烯类混合树脂浸注杨木单板,通过加热聚合对其进行强化改性,考察聚合温度、加热时间、环烷酸钴加入量、氯化锌加入量和偶氮二异丁腈加入量五个树脂液聚合工艺参数对树脂转化率的影响;并利用人工神经网络构建改性工艺与树脂转化率的关系模型,在此基础上对工艺参数进行优化.结果表明,优化后的聚合工艺为聚合温度80 ℃,聚合加热时间7 h,环烷酸估2%,氯化锌6%,偶氮二异丁腈5%,此时转化率达到了69.39%;强化后制备的杨木单板复合材料的表面硬度、耐磨性和静曲强度分别至少提高了1.34倍、2.35倍、1.87倍.
参考文献
| [1] | Shukla K S;Bhatnagar R C .A note on the effect of compression on strength properties of populous deltoids and populous ciliate[J].Journal of Timber Development Association of India,1989,35(01):17-25. |
| [2] | Lawniczak M .Influence of aspen wood density and position in tree on selected properties of wood polystyrene system[J].Holz Als Roh-und Werdstoff,1994,52(01):19-27. |
| [3] | Yildiz UC;Yidiz S;Gezer ED .Mechanical properties and decay resistance of wood-polymer composites prepared from fast growing species in Turkey[J].Bioresource Technology: Biomass, Bioenergy, Biowastes, Conversion Technologies, Biotransformations, Production Technologies,2005(9):1003-1011. |
| [4] | 李华;申宗析 .杨木单板的表面改性与胶合效应[J].林业科学,1990,26(03):247-253. |
| [5] | 王新爱,朱玮,汪玉秀.杨木材性的化学改良技术[J].西北林学院学报,2001(01):76-81. |
| [6] | 王逢瑚,马立军,李永峰,陈广胜,刘志明.强化杨木单板混合树脂液的配比[J].东北林业大学学报,2005(06):45-46. |
| [7] | 王逢瑚,孙建平,李永峰,马立军,陈广胜.混合树脂液强化改性杨木单板的聚合工艺研究[J].林产工业,2007(04):39-42. |
| [8] | 刘焕荣,刘君良,柴宇博.树脂浸渍量对杨木单板层积材性能的影响[J].木材工业,2007(03):11-13. |
| [9] | 孙丰文,张彰.杨木单板苯甲基化改性的研究[J].南京林业大学学报（自然科学版）,2008(06):85-88. |
| [10] | 黄河浪,赵明,董丽君,刘俊,陈雪梅.低温冷等离子体对不同含水率杨木单板表面改性的初步研究[J].林产工业,2010(03):20-22. |
| [11] | 王洋,朱景川,尤逢海,岳洋.基于BP神经网络的TA15钛合金加工图[J].材料热处理学报,2009(02):195-197. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%