以Nb,Si粉末为原料,采用放电等离子烧结(SPS)技术,原位合成了密实的Nb/Nb5Si3复合材料.利用扫描电镜(SEM)、电子探针微区分析(EPMA)和X射线衍射(XRD)等手段对材料的组织结构进行了分析,并探讨了材料的结构形成机制.结果表明,合成的材料由近球状的Nb颗粒与Nb-Nb5Si3共晶组织组成;SPS过程中产生的放电等离子体使Si粉及Nb颗粒的表面熔化,熔融的Nb和Si在冷却过程中发生共晶反应而形成Nb-Nb5Si3共晶体,而未反应完的Nb颗粒则均匀分布在共晶组织中.
参考文献
| [1] | Yeh C L;Chen W H .[J].Journal of Alloys and Compounds,2006,425:216. |
| [2] | Chen Z;Yan Y W .[J].Journal of Alloys and Compounds,2006,413:73. |
| [3] | Geng J;Tsakiropoulos P;Shao G .[J].INTERMETALLICS,2007,15(03):69. |
| [4] | Kim W Y;Hisao T;Akio K .[J].Intermètallics,2001,9(06):521. |
| [5] | Mendiratta M G;Lewandowski J J;Dimiduk D M .[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1991,22A:1573. |
| [6] | 曲士昱,王荣明,韩雅芳.热处理对Nb-10Si合金显微组织的影响[J].航空材料学报,2001(03):9-12. |
| [7] | Sha J;Hirai H;Tabaru T et al.[J].Metallurgical and Materials Transactions,2003,34A:2861. |
| [8] | Chan KS. .Alloying effects on fracture mechanisms in Nb-based intermetallic in-situ composites[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2002(0):513-522. |
| [9] | Chan K S;Davidson D L .[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2003,34A:1833. |
| [10] | 王朋波,杨冠军,毛小南.放电等离子原位烧结制备TiC+TiB/Ti复合材料[J].稀有金属材料与工程,2007(03):484-488. |
| [11] | 陈哲,严有为.原位Nb/Nb5Si3复合材料的放电等离子烧结及结构形成机理[J].稀有金属材料与工程,2006(03):484-487. |
| [12] | 易丹青,杜若昕,曹昱.M5Si3型硅化物的研究及相关的物理冶金学问题[J].金属学报,2001(11):1121-1130. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%