研究了SPS烧结温度对球磨熔体快淬Fe70Cr8Mo2Si5B15粉末的烧结块体合金组织结构与磁性能的影响.结果表明:(1)在30MPa/5min条件下,当烧结温度从850℃提高至1000℃时,样品相对密度从95.8%增加到98.9%;(2)烧结样品主要组成相为α-Fe相,尚存在少量的第二相金属间化合物,且其α-Fe相平均粒晶尺寸处于纳米级范围;(3)随着烧结温度的提高,这些样品合金的比饱和磁化强度σs增加,矫顽力Hc随之降低.
参考文献
| [1] | Kawamura Y;Inoue A;Kojima A et al.Consolidation of Amorphous Fe-Zr-B Powders by Hot-pressing Method[J].Journal of the Japan Society of Powder and Powder Metallurgy,1995,42(01):40-46. |
| [2] | Kojima A;Horikiri H;Kawamura Y et al.Production of nanocrystalline b.c.c. Fe-Nb-B bulk alloys by warm extrusion and their magnetic properties[J].Materials Science and Engineering,1994,A179-A180:511-515. |
| [3] | Shen B L;Kimura H;Inoue A A et al.Consolidation of Fe-Co-Ga-P-C-B Glassy Powders by Spak-Plasma-Sintering and Their Magnetic Properties[J].Journal of the Japan Society of Powder and Powder Metallurgy,2001,48(09):858-862. |
| [4] | 卢斌,易丹青,严彪,殷俊林,刘会群,吴标理,陈小丽,王花宾.高压下Fe84Nb7B9纳米晶软磁块体合金的形成[J].中国有色金属学报,2004(02):173-178. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%