为了制备结构和性能满足骨组织工程支架要求的聚己内酯(PCL)多孔支架材料,采用浸没凝胶相分离法,以冰醋酸和丙酮为混合溶剂,水为凝固剂,壳聚糖(CS)颗粒为添加剂制得一系列PCL多孔支架.探讨了溶剂组成、PCL浓度、CS添加量对PCL多孔支架结构和性能的影响.结果表明:添加CS颗粒有利于形成多孔三维支架,随着CS含量的增加,孔隙率略微下降,抗压强度提高.随着PCL质量分数的增加,孔隙率明显下降.但抗压强度增大.当溶剂组成中丙酮含量为50 Wt%～60 wt%,PCL质量分数不高于10 Wt%时,通过改变CS用量,可制得孔隙率和力学性能满足骨组织工程要求的相互贯通的三维多孔支架材料.
To prepare the poly (ε-caprolactone) (PCL) porous scaffolds whose structure and property could meet the needs of bone tissue engineering,a series of PCL porous scaffolds were prepared by means of the immersion precipitation method using acetic acid and acetone as the blend solvent,distilled water as the quenching bath and chitosan (CS) as the additives.The effects of solvent,PCL concentration and the amount of CS on the structure and property were studied.The results show that the addition of CS is beneficial for forming three-dimensionally porous scaffolds.With the CS amount increasing,the porosity decreases slightly while the compressive strength improves.The porosity decreases obviously with the increasing of PCL mass fraction.When the content of acetone is 50 Wt% ～60 wt% and the content of PCL is below 10 wt%,three-dimensionally porous PCL scaffolds with satisfying porosity and mechanical property could form by adjusting the amount of CS.
参考文献
| [1] | Langer R,Vacanti J P.Tissue engineering[J].Science,1993,260(5110):920-926. |
| [2] | Hollinger J O,Leong K.Poly(alpha-hydroxy acids):Carriers for bone morphogenetic proteins[J].Biomaterials,1996,17(2):187-194. |
| [3] | 王海斌,赫淑倩,赵冬梅.羧甲基壳聚糖/纳米羟基磷灰石复合支架材料的制备及生物安全性[J].复合材料学报,2008,25(6):88-92.Wang Haibin,He Shuqian,Zhao Dongmei.Preparation and biology security of the porous carboxymethyl chitosan/nano hydroxyapatite scaffold biocomposites[J].Acta Materiae Compositae Sinica,2008,25(6):88-92. |
| [4] | Schugens C,Maquet V,Grandfils C,et al.Biodegradable macroporous polylactide implants for cell transplantation Ⅰ:Preparation of polylactide foams by solid-liquid phase separation[J].Polymer,1996,37(6):1027-1038. |
| [5] | 肖秀峰,黄琼瑜,刘榕芳.纳米羟基磷灰石/聚合物多孔复合支架材料[J].复合材料学报,2008,25(6):39-46.Xiao Xiufeng,Huang Qiongyu,Liu Rongfang.Nano-hydroxyapatite/polymer composite porous scaffold materials[J].Acta Materiae Compositae Sinica,2008,25(6):39-46. |
| [6] | Whang K,Thomas C H,Healy K E,Nuber G.A novel method to fabricate bioabsorbable scaffolds[J].Polymer,1995,38(4):837-842. |
| [7] | Whang K,Tsai D C,Nam E K,et al.Ectopic bone formation via rhBMP-2 delivery from porous bioabsorbable polymer scaffolds[J].J Biomed Mater Res,1998,42(4):491-499. |
| [8] | Coombes A G A,Heckman J D.Gel casting of resorbable polymers part 1:Processing and applications[J].Biomaterials,1992,13(4):217-224. |
| [9] | Nam Y S,Yoon JJ,Park T G.A novel fabrication method of macroporous biodegradable polymer scaffolds using gas foaming salt as a porogen additive[J].J Biomed Mater Res,2000,53(1):1-7. |
| [10] | Wu Hua,Wan Ying,Cao Xiaoying.Fabrication of chitosang-polycaprolactone copolymer scaffolds with gradient porous microstructures[J].Materials Letters,2008,62(17/18):2733-2736. |
| [11] | 杨安乐,孙康,吴人洁.聚己内酯的合成改性和应用进展[J].高分子通报,2000(2):52-57.Yang Anle,Sun Kang,Wu Renjie.Synthesis,modiffication and applications of poly (ε-caprolactone)[J].Chinese Polymer Bulletin,2000(2):52-57. |
| [12] | 许树文,吴清基,梁金茹,等.甲壳素纺织品[M].上海:东华大学出版社,2002:21. |
| [13] | Montemhault A,Viton C,Domard A.Physico-chemical studies of the gelation of chitosan in a hydroalcoholic medium[J].Biomaterials,2005,26(8):933-943. |
| [14] | 陆茵,陈欢林,李伯耿.添加剂对PVDF相转化过程及膜孔结构的影响[J].高分子学报,2002(5):656-661.Lu Yin,Chen Huanlin,Li Bogeng.Influence of additives on phase separation process of PVDF solution and membrane morphology[J].Acta Polymerica Sinica,2002(5):656-661. |
| [15] | VandeWitte P,Dijkstra P J,VandenBerg J w A,et al.Metastable liquid-liquid and solid-liquid phase boundaries in polymer-solvent-nonsolvent systems[J].Journal of Polymer Science Part B:Polymer Physics,1997,35(5):763-770. |
| [16] | Young T H,Cheng L P,Lin D J,et al.Mechanisms of PVDF membrane formation by immersion-precipitation in soft (1-octanol) and harsh (water) nonsolvents[J].Polymer,1999,40(19):5315-5323. |
| [17] | 陆茵,陈欢林,李伯耿.制膜条件对PVDF膜形态结构的影响[J].功能高分子学报,2002,15(2):171-176.Lu Yin,Chen Huanlin,Li Bogeng.Effects of preparing condition on PVDF membrane morphology[J].Journal of Functional Polymers,2002,015(2):171-176. |
| [18] | 陆茵,张林,任元龙,汪继忠.溶剂对相分离法制备聚偏氟乙烯微孔膜性质的影响[J].功能高分子学报,2005,18(3):430-433.Lu Yin,Zhang Lin,Ren Yuanlong,Wang Jizhong.Influence of solvents on the PVDF membrane properties[J].Journal of Functional Polymers,2005,18(3):430-433. |
| [19] | Frommer M A,Messalem R M.Mechanism of membrane formation Ⅵ:Convective flows and large void formation during membrane precipitation[J].Ind Eng Chem Prod Res Dev,1973,12(4):328-333. |
| [20] | 左丹英,徐又一,曾秋霞,龚玉洁.浸没沉淀相转化法制备结晶性聚合物微孔膜的研究进展[J].化学通报,2008,71(5):336-342.Zuo Danying,Xu Youyi,Zeng Qiuxia,Gong Yujie.Progress of crystalline polymer membrane prepared by immersion precipitation phase inversion[J].Chemistry Online,2008,71(5):336-342. |
| [21] | Strathmann H,Kock K,Amar P,Baker R W.Formation mechanism of asymmetric membranes[J].Desalination,1975,16(2):179-203. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%