1561铝合金双面双弧TIG焊接接头的组织和力学性能

中国有色金属学报, 2016, 26(10): 2065-2070.

1561铝合金双面双弧TIG焊接接头的组织和力学性能

闫德俊 ^1, , 韩端锋 ^2, , 王毅 ^3, , 罗玖强 ^4, , 刘晓莉 ^5, , 梁志敏 ^6,

1.哈尔滨工程大学船舶工程学院,哈尔滨150003;中船黄埔文冲船舶有限公司,广州510715

2.哈尔滨工程大学船舶工程学院,哈尔滨,150003

3.中船黄埔文冲船舶有限公司,广州,510715

4.中船黄埔文冲船舶有限公司,广州,510715

5.中船黄埔文冲船舶有限公司,广州,510715

6.河北科技大学材料科学与工程学院,石家庄,050018

基金项目: 黄埔区科技计划项目(201518)Project(2013DFR7016) supported by the National International Science and Technology Cooperation Program,China 国防科学技术工业基础研究项目(A0720133002) Project(201518) supported by the Science and Technology Program of Huangpu District,China Project(A0720133002) supported by the Military Industry Basic Research Program,China 国家国际合作项目(2013DFR7016)

关键词：焊接接头 , 双面双弧错位立焊 , 组织非均匀性 , 维氏硬度

Microstructure and mechanical properties of 1561 aluminum alloy joints made by double-sided arc welding

Keywords： welded joint , double-sided dislocation vertical welding , tissue heterogeneity , Vickers hardness

采用双面双弧错位TIG填丝立向焊工艺对1561高镁铝合金进行焊接,并对接头的显微组织和力学性能进行分析.结果表明:焊缝中无气孔和裂纹缺陷;1561铝合金双面双弧错位立向焊缝横截面存在着“人”字形粗晶区,粗晶区两侧和下方有细晶区,同时,在部分熔化区出现了范围较窄的粗晶区;正反面焊道的显微硬度均低于母材的,但热影响区并没有表现出明显的软化现象.焊接接头的抗拉强度达到了母材的90％以上,力学性能良好;接头粗晶区的存在与双面双弧错位TIG焊的温度场和熔池流场有关.

参考文献

[1]	韩善果;闫德俊;刘晓莉;蔡得涛;郑世达;罗玖强.1561铝合金TIG焊接头组织与力学性能分析[J].焊接技术,2015(1):18-21.
[2]	Y. M. Zhang;S. B. Zhang.Double-sided arc welding increases weld joint penetration[J].Welding Journal,19986(6):57-61.
[3]	Y. M. ZHANG.Welding Aluminum Alloy 6061 with the Opposing Dual-Torch GTAW Process[J].Welding Journal,19996(6):0-0.
[4]	Y.B. Zhao;Z.L Lei;Y.B. Chen;W. Tao.A comparative study of laser-arc double-sided welding and double-sided arc welding of 6 mm 5A06 aluminium alloy[J].Materials & design,20114(4):2165-2171.
[5]	刘殿宝;张广军;吴林.大厚板双面双TIG电弧打底焊熔池成形特性[J].焊接学报,2012(3):37-40.
[6]	郭小辉;刘志颖;何刚;王乃友;唐磊.5083铝合金的双枪双面TIG焊工艺和接头性能研究[J].材料开发与应用,2009(5):29-31.
[7]	强伟;王克鸿;林祥礼.铝合金双面双弧同步立焊工艺特征与接头组织性能分析[J].机械工程学报,2015(24):82-89.
[8]	Zhang YM.;Male AT.;Pan C..Solidification behavior of Al-Mg aluminum alloy using double-sided arc welding process[J].Journal of Materials Science Letters,200010(10):831-833.
[9]	张亮;方洪渊;王林森;刘雪松.A7N01铝合金焊接接头的不均匀特性[J].焊接学报,2012(11):97-100.
[10]	Dong HG;Gao HM;Wu L.Heat transfer and fluid flow in fusion type PA-GTA double-sided welding[J].Modelling and simulation in materials science and engineering,20058(8):1205-1215.
[11]	崔旭明;李刘合;张彦华.双面电弧焊接熔透穿透机制[J].航空制造技术,2008(18):85-89,93.
[12]	张平;李奇;赵军军;曾庆强.7A52铝合金中第二相分析及微区电位测试[J].中国有色金属学报,2011(6):1252-1257.
[13]	张国君;刘刚;丁向东;孙军;陈康华.含有不同尺度量级第二相的高强铝合金拉伸延性模型[J].中国有色金属学报,2002(z1):1-10.

上一张下一张

计量

下载量()
访问量()

作者相关

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网