为了生产超低磷钢,在1 600 ℃用高碱度CaO-CaF2-FeO系渣对低磷钢水进行了炉外深脱磷的研究.分析了氧化性和碱度对脱磷效果的影响,确定了合适的渣系组成,测得1 600 ℃下该渣系的磷容量在1018.54～1020.2范围内.实验结果表明:氧化性和碱度是影响脱磷效果的两个制约性因素;在钢水初始磷含量为0.01 %左右的条件下,使用该渣获得了大于50 %的脱磷率及低于0.005 %(最低可达0.002 7 %)的磷含量;在300 t转炉上进行的初步生产试验也获得了50 %左右的脱磷率及0.006 %左右的成品磷含量.
参考文献
| [1] | Borgi C;张炯明.钢水的深脱磷处理[J].国外钢铁,1992(08):25-30. |
| [2] | Kiyohid Hayashi;Masanobu Iikeda;Hideo Katagiri .Dephos-phorization of Liquid Steel by Sodium Carbonate[J].Transactions of the Iron and Steel Institute of Japan,1984,24:207. |
| [3] | 杨吉春;王清华;那树人 等.IF钢水炉外脱磷的实验研究[J].包头钢铁学院学报,1997,16(04):254-258. |
| [4] | H.Ishii;R.J.Fruehan .Dephosphorization Equilibria Between Liquid Iron and Highly Basic CaO-Based Slags Saturated With MgO[J].Iron & Steelmaker,1997(2):47-54. |
| [5] | Shigeko Nakamura;Fumitaka Tsukihashi;Nobuo Sano .Phos-phorus Partition between CaOsatd-BaO-SiO2-FetO Slags andLiquid Iron at 1873 K[J].ISIJ International,1993,33(01):53-58. |
| [6] | Sigwork G K;Elliott J F .The Thermodynamics of Liquid Di-lute Iron Alloys[J].Metal Science Journal,1974,18:298-310. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%