A conventional X-ray difFractometer has been used to determine the -y/y＇ lattice misfit and γ＇ volume fraction for a Ru-containing nickel-based single crystal superalloy at room temperature. The rocking curve was used to characterize the distribution of subgrains. The diffraction peaks obtained by w-20 scan were used to determine the γ/γ＇ lattice misfit and γ＇ volume fraction. A three peaks fitting model was proposed. The peak fitting results are in good agreement with the model. The X-ray diffraction results indicate that the nickel-based single crystal superalloy was not a perfect monocrystalline material, which is comprised of many subgrains; and each subgrain also consists of large numbers of mosaic structures. In addition, two anomalous reflection phenomena were found during the experiment and discussed with respect to their occurrence and impact on the measurement. The experimental results show that the γ/γ＇ lattice misfit and ~/r volume fraction will be various at the different regions of its dendritic microstructure. The average γ/γ＇ lattice misfit and γ＇ volume fraction of the experimental alloy are approximately-0.2% and 70%, respectively. Furthermore, the γ＇ volume fraction calculated by atom microprobe （AP） data is also basically consistent with the experimental results.
参考文献
| [1] | H. Mughrabi .Microstructural aspects of high temperature deformation of monocrystalline nickel base superalloys: some open problems[J].Materials Science and Technology: MST: A publication of the Institute of Metals,2009(2):191-204. |
| [2] | B.MARTY;P.MORETTO;P.GERGAUD .X-RAY STUDY ON SINGLE CRYSTAL SUPERALLOY SRR99: MISMATCH γ/γ', MOSAICITY AND INTERNAL STRESS[J].Acta materialia,1997(2):791-800. |
| [3] | T. Link;A. Epishin .INCREASE OF MISFIT DURING CREEP OF SUPERALLOYS AND ITS CORRELATION WITH DEFORMATION[J].Acta materialia,2000(8):1981-1994. |
| [4] | F. Diologent;P. Caron;T. d'Almeida;A. Jacques;P. Bastie .The γ/γ' mismatch in Ni based superalloys: In situ measurements during a creep test[J].Nuclear Instruments and Methods in Physics Research, Section B. Beam Interactions with Materials and Atoms,2003(0):346-351. |
| [5] | A. Royer .In situ determination of ?' phase volume fraction and of relations between lattice parameters and precipitate morphology in Ni-based single crystal superalloy[J].Acta materialia,1998(15):5357-5368. |
| [6] | C.Y. CUI;Y.F. GU;H. HARADA .Phase Stability and Yield Stress of Ni-Base Superalloys Containing High Co and Ti[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,2006(11):3183-3190. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%