通过计算室温下含硅过饱和钙磷沉积液(SSCPS)中可能形成的各沉积相的过饱和度,对仿生制备含硅羟基磷灰石(Si-HA)的热力学条件进行了分析.结果表明:羟基磷灰石(HA)过饱和度最大;且当pH＜8时,硅不具备以偏硅酸盐形式存在的热力学条件,从而表明SSCPS具备仿生制备Si-HA涂层的热力学可能性.在SSCPS中通过浸泡,在钛表面仿生制备了Si-HA涂层,其Si含量在0.14 at%～1.14 at%,实验验证了热力学分析的正确性;还跟踪了仿生沉积过程pH值变化.
参考文献
| [1] | Albrektsson T;Branemark P I;Hasson H A et al.[J].Acta Orthopaedica Scandinavica,1981,52:155. |
| [2] | Long M;Rack HJ .Titanium alloys in total joint replacement--a materials science perspective.[J].Biomaterials,1998(18):1621-1639. |
| [3] | Kweh S W K;Khor K A;Cheang P .[J].Biomaterials,2002,23:775. |
| [4] | 唐晓恋,刘榕芳,肖秀峰.含硅羟基磷灰石的研究进展[J].硅酸盐通报,2005(06):89-94. |
| [5] | Carlisle E M .[J].Science,1970,167:179. |
| [6] | Ruys A J .[J].Journal of the American Ceramic Society,1993,29:71. |
| [7] | Mochales C;Briak-Ben-Abdeslam H E;Ginebra M P .[J].Key Engineering Materials,2004,254-256:107. |
| [8] | Blasa F;Perez-Pariente J;Vallet-Regy M .[J].Journal of Biomedical Materials Research,2003,66(02):364. |
| [9] | Tang X L;Xiao X F;Liu R F .[J].Materials Letters,2005,59(29-30):3841. |
| [10] | Joná(s)ová L;Müller F A;Helebrant A et al.[J].Biomaterials,2002,23(15):3095. |
| [11] | Kokubo T;Takadama H .How useful is SBF in predicting in vivo bone bioactivity?[J].Biomaterials,2006(15):2907-2915. |
| [12] | 胡岳华.水玻璃与磷灰石、方解石作用的溶液化学研究[J].矿冶工程,1992(02):23. |
| [13] | 邝志清,潘春跃,黄可龙,高鸿儒.Sol-gel法制备羟基磷酸钙超细粉末[J].中南工业大学学报,2000(03):246. |
| [14] | 王勇,高家诚,张亚平,张春艳.钛合金表面仿生矿化的热力学分析[J].稀有金属材料与工程,2004(04):397-399. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%