利用热力学软件计算了齿轮钢氧含量与夹杂物成分的关系、夹杂物转变条件.结果表明,超低氧20CrMoH钢中具有较高塑性的非金属夹杂物成分(质量分数)为:SiO2 0～10%,Al2O3 22%～55%,CaO 42%～60%,MgO 5%～10%,与之平衡的时钢液中铝质量分数在0.020%左右,钙质量分数大于0.7×10-6,氧质量分数在0.000 5%左右.选择组成:w(CaO)>40%,w(Al2O3)≤37%,w(MgO)为10%,(w(CaO)+w(MgO))/w(SiO2)为10,SiO2含量尽量低的渣系,钢中Al2O3、MgO·Al2O3夹杂物可转变为低熔点的钙铝酸盐.
参考文献
| [1] | Hiroki OHTA;Hideaki SUITO .Activities in CaO-MgO-Al_2O_3 Slags and Deoxidation Equilibria of Al, Mg, and Ca[J].ISIJ International,1996(8):983-990. |
| [2] | Sigworth G K;Elliott J F .The Thermodynamics of Liquid Dilute Iron Alloys[J].Metal Science Journal,1974,18:298. |
| [3] | Hideaki SUITO;Ryo INOUE .Thermodynamics on Control of Inclusions Composition in Ultraclean Steels[J].ISIJ International,1996(5):528-536. |
| [4] | 陈襄武.炼钢过程的脱氧[M].北京:冶金工业出版社,1991 |
| [5] | 曲英.炼钢学原理[M].北京:冶金工业出版社,1980 |
| [6] | 张鉴.冶金熔体的计算热力学[M].北京:冶金工业出版社,1994 |
| [7] | 黄希祜.钢铁冶金原理[M].北京:冶金工业出版社,1981 |
| [8] | Todoroki H;Mizuno K .Effect of silica in slag on inclusion compositions in 304 stainless steel, deoxidized with aluminum[J].ISIJ International,2004(8):1350-1357. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%