对超高强度钢A-100带孔构件进行喷丸和孔挤压等表面强化处理,对比在相同试验条件下的疲劳性能,计算分析表面强化延寿增长系数和疲劳极限的提高幅度,获得了超高强度钢A-100带孔构件疲劳的应力集中特性与表面强化改性效果.结果表明,A-100超高强度钢具有很高的应力集中敏感性;表面强化可显著延长带孔构件的疲劳寿命和提高其疲劳极限,表面强化效果主要取决于表面强化层内的残余压应力;疲劳断口分析表明表面强化构件的疲劳源不再位于孔边而是在孔边与内部的过渡部位.由于孔挤压强化在引入较深残余压应力的同时还可以改善孔边的粗糙度,因此其强化效果优于喷丸强化.喷丸和挤压分别使疲劳极限提高了35％和38％,有效缓解了孔边应力集中对疲劳性能的不利影响.
参考文献
| [1] | Japp Schijve.Fatigue of Structures and Materials[M].Springer-Verlag,2009 |
| [2] | Graves J H .Effect of heat treatment on the microstructure and properties of AerMet 100 steel[D].Arrny Research Laboratory,1994. |
| [3] | Volker Schulze.Modern Mechanical Surface Treatment-States,Stability,Effects[M].Wiley-VCH,2006 |
| [4] | Y.K. Gao;X.R. Wu .Experimental investigation and fatigue life prediction for 7475-T7351 aluminum alloy with and without shot peening-induced residual stresses[J].Acta materialia,2011(9):3737-3747. |
| [5] | 高玉魁.喷丸强化对23Co14Ni12Cr3MoE钢疲劳性能的影响[J].材料热处理学报,2007(06):75-77. |
| [6] | 高玉魁.孔挤压强化对23Co14Ni12Cr3MoE钢疲劳性能的影响[J].金属热处理,2007(11):34-36. |
| [7] | Gao, Y.K. .Improvement of fatigue property in 7050-T7451 aluminum alloy by laser peening and shot peening[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2011(10/11):3823-3828. |
| [8] | Mutoh Y;Fair G H;Noble B et al.Waterhoouse.The effect of residual stresses induced by shot-peening on fatigue crack propagation in two high strength aluminum alloys[J].Fatigue and fracture of engineering materials and structures,1987,10:261-272. |
| [9] | Yu-kui Gao;Xiang-bin Li;Qing-xiang Yang .Influence of surface integrity on fatigue strength of 40CrNi_2Si_2MoVA steel[J].Materials Letters,2007(2):466-469. |
| [10] | N. James;D.J. Hughes;Z. Chen .Residual stresses and fatigue performance[J].Engineering failure analysis,2007(2):384-395. |
| [11] | Yu-kui Gao;Mei Yao;Pei-ge Shao .Another Mechanism for Fatigue Strength Improvement of Metallic Parts by Shot Peening[J].Journal of Materials Engineering and Performance,2003(5):507-511. |
| [12] | Y. Gao;F. Lu;M. Yao .Influence of mechanical surface treatments on fatigue property of 30CrMnSiNi2A steel[J].Surface Engineering,2005(4):325-328. |
| [13] | Jeffery L;Roberts .Residual stress effects on fatigue life via the stress intensity parameter,K[D].Dissertation for the Doctor of Philosophy Degree at the University of Tennessee,2002. |
| [14] | Gao Y K;Yao M;Yang Q X et al.Influence of carburization followed by shot peening on fatigue property of 20CrMnTi steel[J].Journal of Materials Engineering and Performance,2005,14(05):591-595. |
| [15] | Gao Y K;Lu F;Yin Y F .Effects of shot peening on fatigue property of 0Cr13Ni8Mo2Al steel[J].Materials Science and Technology,2003,19(03):372-374. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%