以自制的复合磺酸钙基润滑脂为基体，采用硅烷偶联剂表面改性后的纳米铜、纳米镍、纳米二硫化钨和纳米聚酰胺为功能填料，制备了高分子润滑脂涂层。分析了不同聚酰胺添加量对体系的滴点、锥入度和极压性能的影响。结果表明：改性后的功能填料对体系的各项性能都有一定程度的改善，当聚酰胺添加量为2%时，高分子润滑脂涂层的综合性能最优，滴点达到206℃，锥入度达到277(0.1 mm)，极压值达到931 N。
Using self-made calcium sulfonate complex grease as matrix, nanocopper, nanonickel, nano tung-sten disulfide, and nano polyamide powder modified by silane coupling agent as functional fillers, we pre-pared a polymer grease coating. The effects of different amount of polyamide on the drop point, cone penetration, and extreme pressure property were studied. The results show that the modification of funtional fillers can improve the performance to some extent. When the addition amount of polyamide is 2%, the comprehensive properties of the polymer grease coating attain optimum. Its dropping point is 206℃, cone penetration is 277(0.1 mm), and extreme pressure value is 931 N.
参考文献
| [1] | 许立坤.紧固件防护涂镀层技术的发展状况[A].张家界,2007 |
| [2] | 殷跃军,韩长智,夏海渤.达克罗涂层与环氧富铝复合涂层在紧固件表面的防护效果[C].中国表面工程协会第二届达克罗技术产业化论坛论文集,2005:54-61. |
| [3] | 益建国 .复合磺酸钙基润滑脂的结构组成与应用[J].汽车工艺与材料,2005,6(3):41-43. |
| [4] | 刘伟,张天胜.环境友好润滑脂的研究现状与发展前景[J].润滑油,2005(02):26-29. |
| [5] | 白传航.高温丝扣防粘接密封脂的研制[J].合成润滑材料,2005(04):1-4. |
| [6] | 李成菊.微米铜粉在润滑脂中摩擦学性能的考察[J].兰州石化职业技术学院学报,2008(01):24-27. |
| [7] | 王李波,王晓波,刘维民.添加剂Ni-B非晶合金纳米微粒的制备及其摩擦学性能[J].材料保护,2009(05):4-6. |
| [8] | 俸颢,毛大恒.一种二硫化钨高温润滑脂的研制与性能研究[J].重庆师范大学学报(自然科学版),2004(03):50-54. |
| [9] | 熊文,毛大恒,吴尔京.二硫化钨在高温锂基润滑脂中摩擦性能的研究[J].湖南工程学院学报(自然科学版),2004(03):36-39. |
| [10] | 张淑敏,刘太奇.纳米尼龙丝的制备及性能[J].高分子材料科学与工程,2005(05):289-292. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%