通过高能球磨技术制备了Fe78 Si13B9磁性非晶合金粉体,采用XRD和DSC分析了Fe78Si13B9非晶合金粉体的相组成、玻璃转变温度Tg、开始晶化温度Tx和晶化峰温度Tp;利用放电等离子烧结(SPS)技术在不同烧结温度下制备了块体磁性非晶纳米晶合金试样,利用XRD、SEM、Gleeble3500、VSM等分析了不同烧结温度下烧结块体试样的相转变特性、微观形貌、力学性能和磁学性能.结果表明,在500 MPa的烧结压力下,随着烧结温度的升高,烧结试样中的非晶相开始逐渐晶化,烧结试样的致密度、抗压强度、微观硬度、饱和磁化强度均显著提高;在500 MPa的烧结压力和823.15 K的烧结温度下,获得了密度为6.6 g/cm3,抗压强度为1500 MPa,饱和磁化强度为1.3864 T的非晶纳米晶磁性材料.
参考文献
[1] | Xiao Z Y,Tang C Y,Zhao H D,et al.Effects of sintering temperature on microstructure and property evolution of Fe81-Cu2 Nb3Si14 soft magnetic materials fabricated from amorphous melt-spun ribbons by spark plasma sintering technique[J].Journal of Non-Crystalline Solids,2012,358(1):114-118. |
[2] | 张敏,宣天鹏.非晶与纳米晶铁基软磁合金材料的研究现状[J].金属功能材料,2010,17(6):69-72.Zhang Min,Xuan Tianpeng.Current research of amorphous and nanocrystalline Fe-based soft magnetic alloys[J].Metallic Functional Materials,2010,17(6):69-72. |
[3] | Yoshizawa Y,Oguma S,Yamauchi K.New Fe-based soft magnetic alloys composed of ultrafine grain structure[J].Journal of Applied Physics,1988,64(10):6044-6046. |
[4] | Suzuki K,Makino A,Inoue A.Soft magnetic properties of nanocrystalline bcc Fe-Zr-B and Fe-M-B-Cu (M =transition metal) alloys with high saturation magnetization[J].Journal of Applied Physics,1991,70(10):6232-6235. |
[5] | Willard M A,Laughlin D E,Mchenry M E.Structure and magnetic properties of (Fe0.5 Co0.5) 88 Zr7 B4 Cu1 nanocrystalline alloys[J].Journal of Applied Physics,1998,84(12):6773-6777. |
[6] | Takadate K,Kojima A,Mkino A,et al.Effect of Nd substitution on the soft magnetic properties of a nanocrystalline Fe84 Nb7 B9 alloy[J].Scripta Materialia,2001,44(8/9):1401-1405. |
[7] | Li X,Makina A,Kato H,et al.Fe76 Si9.6 B8.4 P6 glassy powder soft-magnetic cores with low core loss prepared by spark plasma sintering[J].Materials Science and Engineering B,2011,176(15):1247-1250. |
[8] | Benjamin J S,Bomford M J.Dispersion strengthened aluminum made by mechanical alloying[J].Metallurgical Transactions A,1977,8A(8):1302-1305. |
[9] | Lu I R,Moelle C,Sagel A,et al.Preparation and thermal stability of ceramic/metallic glass composites prepared by mechanical alloying[J].Materials Letters,1998,35 (5/6):297-302. |
[10] | 王松,谢明,张吉明,等.放电等离子烧结技术进展[J].贵金属,2012,33(3):73-77.Wang Song,Xie Ming,Zhang Jiming,et al.Development of spark plasma sintering technology[J].Precious Metals,2012,33(3):73-77. |
[11] | Gao W J,Jia C C,Jia X,et al.Effect of processing parameters on the microstructure and thermal conductivity of diamond/Ag composites fabricated by spark plasma sintering[J].Rare Metals,2010,29(6):625-629. |
[12] | 庾正伟,刘颖,李 军,等.放电等离子烧结制备FeSiB块体非晶合金[J].稀有金属材料与工程,2009,38(S1):44-47.Yu Zhengwei,Liu Ying,Li Jun,et al.Fabrication of FeSiB bulk metallic glasses by spark plasma sintering[J].Rare Metal Materials and Engineering,2009,38 (S1):44-47. |
[13] | Herzer G.Grain size dependence of coercivity and permeability in nanocrystalline ferromagnets[J].IEEE Transactions on Magnetics,1990,26(5):1397-1402. |
[14] | 唐翠勇,肖志瑜,马春宇,等.机械合金化制备Fe94-xZr2 Nb4 Bx(x=10,1 5,20)纳米合金粉及磁性研究[J].稀有金属材料与工程,2011,40(S2):300-304.Tang Cuiyong,Xiao Zhiyu,Ma Chunyu,et al.Magnetic properties of Fe94-xZr2Nb4Bx (x =10,15,20)nanocrystalline alloy powders prepared by mechanica alloying[J].Rare Metal Materials and Engineering,2011,40 (S2):300-304. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%