Intragranular ferrite was formed at inclusions in a vanadium microalloyed steel with excess amount of sulfur. The chemical composition of inclusions in the steel was analyzed by SEM-EDS. The inclusions were mainly composed of MnS and aluminum oxides. The precipitation of MnS at aluminum oxides might result in Mn depletion, which, in turn, promotes the formation of intragranular ferrite. Optical and SEM observations and threedimensional (3D) reconstruction demonstrated that intragranular ferrite was formed at inclusions. The morphology of intragranular ferrite changed with undercooling. At higher temperatures intragranular ferrite was nearly equiaxed whereas it was plate-like or lath-like at lower temperatures.
参考文献
| [1] | M Enomoto.[J].Metals and Materials:115. |
| [2] | T.Maki .[Z].Tetsu-to-Hagané,1995. |
| [3] | S W Yang;X M Wang;C J Shang.[J].Journal of University of Science and Technology Beijing(English Edition):214. |
| [4] | H Mabuchi;R Uemori;M Fujioka.[J].ISIJ International,1996:80. |
| [5] | J M Gregg;H K D H Badeshia.[J].Acta Materialia:739. |
| [6] | J H Shim;Y W Cho;S H Chung;J D Shim,D N Lee.[J].Acta Materialia:2751. |
| [7] | J. -H. SHIM;Y. -J. OH;J. -Y SUH .FERRITE NUCLEATION POTENCY OF NON-METALLIC INCLUSIONS IN MEDIUM CARBON STEELS[J].Acta materialia,2001(12):2115-2122. |
| [8] | S.Zhang .Ferrite Nucleation at Ceramic/Austenite Interfaces[J].ISIJ International,1996(10):1301-1309. |
| [9] | K Sumino .Internal Report,Physical Metallurgy of Fine Inclusions[R].Forum,ISIJ,1997. |
| [10] | P Krauklis;F J Barbaro;K E Easterling.Proc.Int.Conf Martensitic Transformations[C].Monterey Institute for Advanced Studies,Monterey,1993:439. |
| [11] | Z Zhang;R A Farrar.[J].Materials Science and Technology:237. |
| [12] | F Ishikawa;T Takahashi;T Ochi.[J].Metallurgical and Materials Transactions:929. |
| [13] | J Yamaguchi;T Furuhara;T Maki.[J].CAMP-ISIJ:1312. |
| [14] | Use of Fine Inclusions in Microstructure Control of Steels[R].Final Report of Inclusions Committee,The Iron and Steel Institute of Japan,1995. |
| [15] | M. V. Kral;G. Spanos .THREE DIMENSIONAL MORPHOLOGY OF CEMENTITE PRECIPITATES[J].Scripta materialia,1997(8):875-882. |
| [16] | T L Wolfsdorf;W H Bender;P W Voorhees .[J].Acta Materialia,45:2279. |
| [17] | M A Mangan;M V Kral;G Spanos .[J].Acta Materialia,47:4263. |
| [18] | K.M. Wu;M. Enomoto .Three-dimensional morphology of degenerate ferrite in an Fe-C-Mo alloy[J].Scripta materialia,2002(8):569-574. |
| [19] | K M Wu;M Kagayama;M Enomoto.[J].Materials Science and Engineering:143. |
| [20] | K. M. WU;T. YOKOMIZO;M. ENOMOTO .Three-dimensional Morphology and Growth Kinetics of Intragranular Ferrite Idiomorphs Formed in Association with Inclusions in an Fe-C-Mn Alloy[J].ISIJ International,2002(10):1144-1149. |
| [21] | K M Wu;M Enomoto.[J].Acta Metallurgica Sinica(Eng Lett):169. |
| [22] | K M Wu;Y Inagawa;M Enomoto.[J].Materials Characterization:121. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%