采用化学气相沉积技术,以甲烷作为碳源,在核石墨IG-110基体上制备层状热解炭涂层。利用偏光显微镜、扫描电子显微镜( SEM)、透射电子显微镜( TEM)以及同步辐射掠入射X 射线衍射( GI-XRD)研究热解炭涂层的微观结构和生长特性。结果表明,热解炭涂层具有大锥体、小锥体和再生锥体三种生长锥微观结构,热解炭片层间结合紧密,生长锥间结合密实。热解炭涂层存在光滑层和再生层两种织构,每种织构都含有两种晶面间距不同的相结构,平滑层主要含有低石墨化度相,而再生层主要含有高石墨化度相。热解炭涂层致密的微观结构和仅存在的纳米级别的微孔使其可以作为气体阻隔涂层。
The molten salt reactor ( MSR) is one of the six Generation IV reactors that is being reexamined today, owing to its unique fuel cycle capabilities and safety characteristics. IG-110 nuclear graphite a candidate material for constructing a MSR. However, the existence of large pores at its surface is a big problem due to the impregnation of molten salts and the diffusion of fission product gases into the graphite through the pores. A pyrolytic carbon ( PyC) coating can act as a barrier coating on the nuclear graphite. Investigation of the microstructure and growth characteristics of PyC is very important for an understanding of the relationship between microstructure and performance. In this study, polarized light microscopy, scanning electron microscopy, transmission electron microscopy and synchrotron based grazing incidence X-ray diffraction were used to study the microstructure and growth characteristics of the PyC coating. Results show that the PyC coating shows three growth cones ( a large cone, a smaller one and a regenerative cone) and exhibits a wave-like layered structure. The resulting structure is fairly dense. There are two kinds of textures in the PyC coating:smooth laminar and regenerative laminar, each of which contains two crystal structures with different interlayer spacings. The smooth laminar carbon has mostly a low degree of graphitization, while the regenerative laminar structure mainly has a high degree of graphitization. The PyC coating is a perfect barrier to gas infiltration due to its compact structure and it containing only nanopores rather than large pores.
参考文献
[1] | DoE US .A technology roadmap for generation IV nuclear energy systems[ USDOE/GIG-002-00][R].Washington,D.C,2002. |
[2] | Forsberg C W.Molten-salt-reactor technology gaps[A].,2006:4-8. |
[3] | Burchell T D.Carbon Materials for Advanced Technologies[M].Elsevier science,1999 |
[4] | Rosenthal M W;Kasten P R;Briggs R B .Molten salt reactors-history,status,and potential[J].Nuclear Applications and Technology,1970,8(2):107-117. |
[5] | Briggs R B .Molten salt reactor program semiannual progress re-port for period ending february 28[ Technical Report ORNL-3936][R].Oak Ridge National Laboratory,1966. |
[6] | Rosenthal M W;Haubenreich P N;Briggs R B .The develop-ment status of molten-salt breeder reactors[ Technical Report ORNL-4812][R].Oak Ridge National Laboratory,1972. |
[7] | Feng, S.;Xu, L.;Li, L.;Bai, S.;Yang, X.;Zhou, X. .Sealing nuclear graphite with pyrolytic carbon[J].Journal of Nuclear Materials: Materials Aspects of Fission and Fusion,2013(1/3):449-454. |
[8] | 周伟敏,徐南华.聚焦离子束(FIB)快速制备透射电镜样品[J].电子显微学报,2004(04):513-513. |
[9] | Coffin I F .Structure-property relations for pyrolytic graphite[J].Journal of the American Ceramic Society,1964,47(10):473-478. |
[10] | 孟广耀.化学气相淀积与无机新材料[M].北京:科学出版社,1984 |
[11] | Wan-Chang Sun;He-Jun Li;Hong-Mei Han .Microstructure of the pyrocarbon matrix prepared by the CLVI process[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2004(1/2):245-249. |
[12] | 周序科,徐红军.热解石墨的形貌结构及缺陷[J].炭素,2000(02):16-22. |
[13] | Bourrat X.;Fillion A.;Naslain R.;Chollon G.;Brendle M. .Regenerative laminar pyrocarbon[J].Carbon: An International Journal Sponsored by the American Carbon Society,2002(15):2931-2945. |
[14] | Agnes Oberlin .Pyrocarbons[J].Carbon: An International Journal Sponsored by the American Carbon Society,2002(1):7-24. |
[15] | Bourrat X;Trouvat B;Limousin G et al.Pyrocarbon anisotro-py as measured by electron diffraction and polarized light[J].Journal of Materials Research,2000,15(1):92-101. |
[16] | Diefendorf R;Tokarsky E .Air force report[ AF33(615)-70-C-1530][R].,1971. |
[17] | B. Reznik;K.J. Huttinger .On the terminology for Pyrolytic carbon[J].Carbon: An International Journal Sponsored by the American Carbon Society,2002(4):621-624. |
[18] | V.De Pauw;B.Reznik;S.Kalhofer;D.Gerthsen;Z.J.Hu;K.J.Huttinger .Texture and nanostructure of pyrocarbon layers deposited on planar substrates in a hot-wall reactor[J].Carbon: An International Journal Sponsored by the American Carbon Society,2003(1):71-77. |
[19] | Wilson M J.A Handbook of Determinative Methods in Clay Mineralogy[M].Blackie, London,1987 |
[20] | Toney M F;Huang T C;Brennan S et al.X-ray depth profi-ling of iron oxide thin films[J].Journal of Materials Research,1988,3(02):351-356. |
[21] | Neerinck DG.;Vink TJ. .DEPTH PROFILING OF THIN ITO FILMS BY GRAZING INCIDENCE X-RAY DIFFRACTION[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,1996(1/2):12-17. |
[22] | Lim G;Parrish W;Ortiz C et al.Grazing incidence synchro-tron x-ray diffraction method for analyzing thin films[J].Jour-nal of Materials Research,1987,2(4):471-477. |
[23] | Vineyard G .Grazing-incidence diffraction and the distorted-wave approximation for the study of surfaces[J].Physical Review B,1982,26(8):4146-4159. |
[24] | Reynier Y;Yazami R;Fultz B et al.Evolution of lithiation thermodynamics with the graphitization of carbons[J].Journal of Power Sources,2007,165(2):552-558. |
[25] | Tzeng SS.;Chr YG. .Evolution of microstructure and properties of phenolic resin-based carbon/carbon composites during pyrolysis[J].Materials Chemistry and Physics,2002(2/3):162-169. |
[26] | Zaldivar R J;Rellick G S .Some observations on stress graphiti-zation in carbon-carbon composites[J].CARBON,1991,29(8):1155-1163. |
[27] | 晋勇;孙小松;薛屺.X 射线衍射分析技术[M].北京:国防工业出版社,2008 |
- 下载量()
- 访问量()
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%