以片状结构的高岭土、滑石、工业氧化铝为原料在1350 ℃×2 h的温度下合成堇青石粉体.结果表明:利用含杂质较少的片状结构的高岭土比含杂质较多的苏州土合成的堇青石粉体纯度更高,从XRD及SEM图谱中可以观察到合成的堇青石呈片状结构.针对堇青石成核困难的问题,实验中加入一定量的堇青石熟料作为晶核剂可促进堇青石的生成,使反应更加完全,并且降低了堇青石的热膨胀系数.
参考文献
| [1] | Chen Y Q;Wu K Z;Wang L X.The Synthesis and Application of Cordierite[J].China Ceramics,1992(05):38-43. |
| [2] | Toshiyuki Hamanaka .Cordierite Honeycomb Strut rue bBody and Method of Producing the Same[P].US 4877 670,1989-10-31. |
| [3] | Du Y J;Li P .Ways to Decrease the Thermal Expansion of Cordierite Honeycomb Structural Body[J].Naihuocailiao,1999,33(06):351-354. |
| [4] | 张华,胡娟,周万城,罗发.堇青石质蜂窝陶瓷的制备[J].硅酸盐学报,2004(01):24-28. |
| [5] | Landon T E .Method of Preparing Crack-free Monolithic Polycrystalline Cordierite Substrates[P].US 4001028,1977-01-04. |
| [6] | Locker R J;Murtagh M J .Verfahrenzur Herstellung Eines Cordientkorpers[P].DE 4339172,1994-05-26. |
| [7] | Matsuhisa T;Soejima S;Yamamoto N .Cordierite Ceramics Honeycomb and a Method for Producing the Same[P].US 4295892,1981-10-20. |
| [8] | 段满珍,杨立荣,陈嘉庚.影响合成堇青石材料热膨胀系数的因素[J].耐火材料,2007(03):201-204. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%