In an aqueous solution of the mixtures of γ-amino propyl triethoxy silane and γ-glycidoxy propyl trimethoxy silane, a composite silane conversion coating was developed on galvanized steel. FESEM (field emission scanning electron microscope), XPS (X-ray photoelectron spectroscopy), ATR FTIR (attenuated total reflection Flourier transform infrared spectroscopy) and SST (salt spray test) were used to characterize the obtained composite silane conversion coating and also the coating formation process was studied. The result showed that the surface of the composite silane conversion coating was complete, consecutive and compact. The coating could endure a neutral salt spray test for 72 h without corrosion. The result of salt spray test indicated that the composite silane conversion coating can provide a better corrosion inhibition than the coating which was composed of the single silane. Based on observation and analysis, it was proposed that the formation process of the silane coating on zinc should consist of three steps: the hydrolysis of the silane molecules, silane chemical adsorption and silane crosslinking condensation. The crosslinking reactions took place between ~'-amino propyl triethoxy and "/-glycidoxy propyl trimethoxy silane during the forming process of the coating, and a high crosslinked density interpenetrating structure network was obtained, so the composite silane conversion coating could keep the corrosive substances from the zinc more effectively.
参考文献
| [1] | Hultzsch K C;Nelson J M;Lough A] et al.Synthesis,Characterization,and Homopolymerization and Copolymeriza tion Behavior of the Silicon-Bridged [1]Chromarenophane Cr(.eta.C6Hs )2SiMe[J].Organometallics,1995,14(12):5496. |
| [2] | Cuence T;Royo P .Transition Metal Complexes With Func tionalized Silyl-Substituted Cyclopentadienyl and Related Lig ands:Synthesis and Reactivity[J].Coordination Chemistry Reviews,1999,193(11):447. |
| [3] | Zhu DQ.;van Ooij WJ. .Corrosion protection of metals by water-based silane mixtures of bis-[trimethoxysilylpropyl]amine and vinyltriacetoxysilane [Review][J].Progress in Organic Coatings: An International Review Journal,2004(1):42-53. |
| [4] | Ji WG;Hu JM;Liu L;Zhang JQ;Cao CN .Improving the corrosion performance of epoxy coatings by chemical modification with silane monomers[J].Surface & Coatings Technology,2007(26):4789-4795. |
| [5] | Zhu D Q;Van Ooij W J .Corrosion Protection of AA 2024-T3 by Bi-[ 3-(Triethoxysilyl)Propyl]Tetrasulfide in Sodium Chloride Solution:Part 2:Mechanism for Corrosion Protection[J].Corrosion Science,2003,45(10):2177. |
| [6] | Wang H M;Akid R .A Room Temperature Cured Sol-Gel An-ticorrosion Pre-Treatment for A1 2024-T3 Alloys[J].Corro-sion Science,2007,49(12):4491. |
| [7] | Han YH;Taylor A;Knowles KM .Characterisation of organic-inorganic hybrid coatings deposited on aluminium substrates[J].Surface & Coatings Technology,2008(9):1859-1868. |
| [8] | Montemor M F;Pinto R;Ferreira M G S .Chemical Composi-tion and Corrosion Protection of Silane Conversion Coatings Modified With CeOz Nanoparticles[J].Electrochimica Acta,2009,54(22):5179. |
| [9] | Flis J;Kanoza M .Electrochemical and Surface Analytical Stud-y of Vinyl-Triethoxy Silane Conversion Coatings on Iron After Exposure to Air[J].Electrochimica Acta,2006,51(11):2338. |
| [10] | Montemor M.F.;Simoes A.M. .The corrosion performance of organosilane based pre-treatments for coatings on galvanised steel[J].Progress in Organic Coatings: An International Review Journal,2000(1):17-26. |
| [11] | WU Jin guang.FTIR Technology and Applications in Recent Years[M].北京:科学技术文献出版社,1994 |
| [12] | LIU Yun.Organic Analysis[M].Changchun:Jilin Universi ty Press,1992 |
| [13] | Li H Y;Wang R G;Hu H L et al.Surface Modification of SelbHealing Poly(Urea-Formaldehyde)Microcapsules Using Silane Coupling Agent[J].Applied Surface Science,2008,255(05):1894. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%