为了减少电火花加工(EDM)工具电极的损耗,采用稀土La2O3为电铸基液添加剂,制备了Cu-SiC复合材料.电铸液组成和工艺条件为:CuSO4.5H2O 200 g/L,H3BO320g/L,NaCl 80 mg/L,SiC 35 g/L,La2O3≤2.5 g/L,温度30℃,电流密度4 A/dm2,时间5h.研究了La2O3添加量不同时,电铸Cu-SiC复合材料中SiC的分布情况和沉积量,以及将其用作EDM工具电极时的表面形貌和相对质量损耗.结果表明,La2O3可促进SiC颗粒与铜共沉积,改善SiC在电铸层中的分散性,提高铸层的抗电蚀性.当La2O3添加量为1.5 g/L时,电铸Cu-SiC复合材料的抗电蚀性最佳.
参考文献
| [1] | Thomas R. Newton;Shreyes N.Melkote;Thomas R. Watkins;RosaM.Trejo;Laura Reister.Investigation of the effect of process parameters on the formation andcharacteristics of recast layer in wire-EDM of Inconel 718[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2009:208-215. |
| [2] | Jayakumar Narasimhan;Zuyuan Yu;Kamlakar P. Rajurkar .Tool Wear Compensation and Path Generation in Micro and Macro EDM[J].Journal of manufacturing processes,2005(1):75-82. |
| [3] | 杨建明,卢龙,李映平.电火花加工工具电极制备技术研究进展[J].机床与液压,2007(11):151-154,157. |
| [4] | Xiaodong Yang;Chunwei Xu;Masanori Kunieda .Miniaturization of WEDM using electrostatic induction feeding method[J].Precision Engineering,2010(2):279-285. |
| [5] | 兰明明,薛玉君,段明德,马伟,李济顺.脉冲电铸制备纳米CeO2增强镍基复合材料[J].机械工程材料,2009(01):33-36. |
| [6] | 明平美,朱荻,曾永彬,朱健,贾世星.纳米氧化镧对电铸电极材料抗电蚀性的影响[J].稀土,2006(03):20-23,64. |
| [7] | 刘敏娜,高德淑,李朝晖,雷钢铁.稀土氧化物对镀铬溶液性能的影响[J].湘潭大学自然科学学报,2000(04):65-67. |
| [8] | 段智鹏 .基于氧化镧的电铸EDM铜电极制备及试验研究[D].山东理工大学,2012. |
| [9] | 郭忠诚 .稀土对复合镀工艺及镀层性能的影响[J].金属学报,1996,32(5):516-520. |
| [10] | 雷卫宁,朱荻,朱增伟.纳米La2O3对精密电铸过程的影响与分析[C].2005年中国机械工程学会年会,2005:974-978. |
| [11] | 明平美,朱荻,胡洋洋,曾永彬.超声微细电铸试验研究[J].中国机械工程,2008(06):644-647. |
| [12] | 李丽,殷凤仕,牛宗伟,袁光明.电沉积Cu基SiC复合电极材料[J].功能材料,2013(08):1188-1190. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%