以丙烯酸及丙烯酸酯类单体为原料,在预聚过程中加入自制的改性纳米硅溶胶,采用溶液聚合法制备了改性纳米硅溶胶-丙烯酸树脂复合乳液,研究了反应时间、m(引发剂)/m(单体)和m(SiO2)/m(单体)对复合乳液稳定性及其漆膜性能的影响.结果表明,反应时间为4h、m(引发剂)/m(单体)为3％、m(SiO2)/m(单体)为5％时,复合乳液的综合性能最优.与市售产品相比,所制备的改性纳米硅溶胶-丙烯酸树脂复合乳液涂膜性能更优,其硬度为4H,附着力0级,冲击强度50 kg.cm,柔韧性2 mm.
参考文献
| [1] | 刘国杰,杨宝.丙烯酸树脂及涂料研究与开发的一些新进展[J].现代涂料与涂装,2012(08):6-10. |
| [2] | Zafar S;Riaz U;Ahmad S .Water-borne melamine-formaldehyde-cured epoxy-acrylate corrosion resistant coatings[J].Journal of Applied Polymer Science,2008(1):215-222. |
| [3] | 管建军;强西怀;钱亦萍 等.改性丙烯酸树脂皮罩涂饰刑的研究进展[J].中国反革,2007,36(11):56-60. |
| [4] | Urska Sebenik;Janvit Golob;Matjaz Krajnc .Comparison of properties of acrylic-polyurethane hybrid emulsions prepared by batch and semibatch processes with monomer emulsion feed[J].Polymer international,2003(5):740-748. |
| [5] | 王晓明 .水性丙烯酸树脂涂料的研究[D].南京航空航天大学,2012. |
| [6] | S. Ozgumus;T. B. Iyim;I. Acar;E. Kucukoglu .Synthesis of novel silicone modified acrylic resins and their film properties[J].Polymers for Advanced Technologies,2007(3):213-219. |
| [7] | Jia, MQ;Wu, CB;Li, W;Gao, DH .Synthesis and Characterization of a Silicone Resin with Silphenylene Units in Si-O-Si Backbones[J].Journal of Applied Polymer Science,2009(2):971-977. |
| [8] | 游胜勇,陈衍华,谌开红,程斌.纳米硅溶胶改性聚硅氧烷微乳液的研究[J].涂料工业,2014(01):12-17. |
| [9] | 张莹娇,陈姚,于欣伟,王步华,秦中海,蔡晓敏.硅溶胶/有机硅改性丙烯酸树脂复合材料的制备[J].电镀与涂饰,2014(02):66-69. |
| [10] | LIU Y L;HSU C Y;HSU K Y .Poly(methylmethacrylate)-silica nanocomposites films from surfaee-functionalized silica nanoparticles[J].POLYMER,2005,46(6):1851-1856. |
| [11] | 徐瑞芬,佘广为.原位聚合法制备纳米TiO2/有机硅改性丙烯酸酯复合乳液[J].有机硅材料,2003(06):11-14. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%