采用活性模板法制备了高纯纳米镍(Ni)粉体.研究了影响纳米粉体性能的各种因素,通过X射线衍射(XRD)、透射电子显微镜(TEM)和激光粒度分析仪等手段对样品的成分、形貌、粒度及其分布进行了分析,探讨了活性模板的作用机理.结果表明:模板介质炭黑具有微反应器作用、空间位阻效应和较强的还原性,活性模板法制得的纳米Ni粉呈规则的球形链状分布,无明显团聚体,平均粒径为45.7 nm,粒径分布窄,粒径范围在16.0 nm～59.1 nm.
参考文献
| [1] | 张立德;牟季美.纳米材料和纳米结构[M].北京:科学出版社,2001:2-6. |
| [2] | 魏智强,温贤伦,王君,吴志国,徐建伟,吴现成,闫鹏勋.工艺参数对阳极弧放电等离子体制备镍纳米粉的影响[J].稀有金属材料与工程,2004(03):305-308. |
| [3] | Saito Y;Mihama K;Uyeda R .Formation of Ultrafine Metal Particles by Gas-Evagaration[J].Japanese Journal of Applied Physics,1980,19:1603-1610. |
| [4] | Marignier J L;Belloni J;Delcourt M O et al.Microaggregates of Non-Noble Metals and Bimetallic Alloys Prepared by Radiation-Induced Reduction[J].Letters To Nature,1985,317:344-345. |
| [5] | Nagashima K;Wada M;Kato A .Preparation of Fine Ni Particles by the Spray-Pyrolysis Technique and Their Film Forming Properties in the Thick Film Method[J].Journal of Materials Research,1990,5(12):2828-2834. |
| [6] | Matsunawa A;Katayama S .Laser Production of Ultrafine Powders[J].Annales de Chimie Science des Materiaux,1993,18(5-6):379-386. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%