为了预防和消除横裂纹,传统的方法是采用高温避开法或低温避开法,使得在弯曲或矫直操作时铸坯的表面温度避开二冷低延性温度范围,但实践证明,传统的方法并不能从根本上消除裂纹的产生.在总结传统冷却模式缺点的前提下,详细介绍了日本住友金属开发的1种新的冷却工艺制度即SSC冷却模式,并分析了SSC冷却模式与传统冷却模式对铸坯高温力学性能和裂纹敏感性的影响.
参考文献
| [1] | 袁伟霞;韩志强;蔡开科 等.连铸板坯凝固过程应变及内裂纹研究[J].炼钢,2001,17(02):48-51. |
| [2] | A. S. Normanton;B. Barber;A. Bell .Developments in online surface and internal quality forecasting of continuously cast semis[J].Ironmaking & Steelmaking: Products and applications,2004(5):376-382. |
| [3] | Akihiko KUSANO;Hideyuki MISUMI .Estimation of the Formed Position of the Surface Cracks on the Slab in the Continuous Caster[J].鉄と鋼,1996(1):35-40. |
| [4] | Akihiko KUSANO;Hideyuki MISUMI;Sinzo HARADA .The mechanism of the internal oxidation layer along the surface crack on the slab[J].Tetsu To Hagane-Journal of the Iron and Steel Institute of Japan,1995,81:52. |
| [5] | H.Yasunaka;K.Nakayama;K.Ebina et al.Improvement of transverse corner cracks in continuously cast hypoperitectic slabs[J].Tetsu To Hagane-Journal of the Iron and Steel Institute of Japan,1995,9:894-899. |
| [6] | 王新华,王文军,刘新宇,费惠春,张立,叶锦渭.减少含铌、钒、钛微合金化钢连铸板坯角横裂纹的研究[J].钢铁,1998(01):22-25. |
| [7] | Toru KATO;Yoshiki ITO;Masayuki KAWAMOTO .Prevention of Slab Surface Transverse Cracking by Microstructure Control[J].ISIJ International,2003(11):1742-1750. |
| [8] | H.G.SUZUKI;Satoshi NISHIMURA;Jun IMAMURA et al.Embrittlement of steels occurring in the temperature range from 1 000 to 600 ℃[J].Transactions of the Iron and Steel Institute of Japan,1984,24:169-177. |
| [9] | 史宸兴.实用连铸冶金技术[M].北京:冶金工业出版社,1998 |
| [10] | 蔡开科;程士富.连续铸钢原理及工艺[M].北京:冶金工业出版社,1994 |
| [11] | 蔡开科.连铸坯裂纹与钢的高温力学行为[J].连铸,1990(06):2. |
| [12] | Young Mock Won;Kyung-hyun Kim;Tae-jung Yeo .Effect of cooling rate on ZST,LIT and ZDT of carbon steel near melting point[J].ISU International,1998,38(10):1093-1099. |
| [13] | 高兴健 .连铸板坯高温力学性能研究及二冷工艺制度分析[D].重庆大学,2009. |
| [14] | Barrie MINTZ .The Influence of Composition on the Hat Ductility of Steels and to the Problem of Transverse Cracking[J].ISIJ International,1999(9):833-855. |
| [15] | B.Minz;R.Abu-Shosha;M.Shaker .Influence of deformation induced ferrite,grain boundary sliding,and dynamic recrystallisation on hot ductility of 0,1 %～0.75 % C steel[J].Materials Science and Technology,1993,9(10):907-914. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%