用扫瞄电镜在拉伸试样断口心部,测量了BHW60钢在20,-60,-100和-140℃下的临界空穴扩张比R_e/R_o,研究了它与宏观断裂韧性V_GC的关系以及热处理状态的影响结果表明:(1)同一温度下R_e/R_o的测量值大致遵循正态概率分布;(2)R_e/R_o随着温度降低直线减小; (3)R_e/R_o与V_GC的关系为V_GC=Cln(R_e/R_o),其中C≈3.5,与R—T空穴扩张模型符合得较好,H与温度和热处理状态无关
The critical void-grwoth ratio, R_c/ R_o, was measured quantitatively underSEM to the core of fracture surface of smooth and notched tensile specimens for BHW60steel at 20, -60, -100 and -140℃. Correlation between R_c/ R_0 and macroscopic fracturetoughness, V_(GC), as well as the effect of heat treated condition upon them were investigated.Results show that the R_c/ R_0 values are approximately obedient to normal probability dis-tribution at the same temperature, decrease linearly with the decrease of temperature and arerelated to V_(GC) as: V(GC)= Cln(R_c/ R_0), where C=3.5. This expression seems to be in goodagreement with the R-T model of void-grwoth and the coefficient C is insensitive to temper-ature and heat treated condition.
参考文献
| [1] | |
| [2] | |
| [3] | |
| [4] | |
| [5] | |
| [6] |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%