采用固相法成功制备了纯度较高的各向异性负热膨胀材料Sc2W3O12。将ZrO2与Sc2W3O12按一定体积比混合，在1200℃烧结10h制备Sc2W3O12／ZrO2复合材料。通过XRD、SEM、EDS和热膨胀仪对合成样品的晶体结构、断面形貌和热膨胀性能进行表征。结果表明：样品组元为正交相Sc2W3O12和单斜相Z2O2；在30-600℃内，Sc2W3O12／ZrO2复合材料的热膨胀系数皆线性一致，并且通过改变Sc2W3O12的体积分数，其热膨胀系数可以控制为正、负或零，其中60％Sc2W3O12／ZrO2复合材料在30-600℃的平均热膨胀系数为0．026×10^-6℃^-1，近似为0。
Sc2W3O12, which exhibits excellent anisotropic negative thermal expansion was synthesized using solid- state reaction. Sc2W3 O12/ZrO2 composites were prepared by mixing ZrO2 and Sc2 W3 O12 at different volume ratios and sintered at 1200 ℃ for 10 h. The crystal structure, fracture surface morphology and thermal expansion properties of the synthesized samples were characterized by XRD, SEM, EDS and dilatometer. The results indicate that the obtained samples contain only orthorhombic Sc2W3O12 and monoclinic ZrO2 phase. All the thermal expansion properties of Sc2W3O12/ZrO2 composites are linear from 30 ℃ to 600 ℃, and their thermal expansion coefficients can be controlled as positive, negative or even zero by adjusting the volume fraction of Sc2W3012. 60%Sc2 W3 O12/ZrO2 composite shows almost zero thermal expansion, and its average thermal expansion coefficient is0.026×10^-6℃^-1 from 30℃ to 600℃.
参考文献
| [1] | Evans J SO, Mary T A, Sleight A W, Negative thermal expansion in a large molybdate and tungstate family [J]. J Solid State Chem, 1997, 133: 580-583. |
| [2] | 关振铎,张中太,焦金生.无机材料物理性能[M].北京:清华大学出版社,1992:127. |
| [3] | Mary T A, Evans J S O, Vogt T, et al. Negative thermal expansion from 0. 3 to 1050 Kelvin in ZrW208 [J]. Scienee, 1996, 272(5): 90-92. |
| [4] | Niwa E, Wakamiko S, Ichikawa T, et al. Preparation of dense ZrW2O8/ZrO2 cosintered ceramics with controlled thermal expansion coefficients [J].J Ceram Soc Jpn, 2004, 112(5): 271-275. |
| [5] | Lommens P, De Meyer C, Bruneel E, et al. Synthesis and thermal expansion of ZrO2/ZrW208 composites [J].J Eur Ceram Soc, 2005, 25: 3605-3610. |
| [6] | 杨新波,程晓农,严学华.ZrWzO8/Zr02可控热膨胀复合材料的制备[J].复合材料学报,2007,24(3):148-153. |
| [7] | 张志萍,刘红飞,程晓农.原位反应固相法合成低热膨胀ZrW2O8/ZrO2复合材料[J].功能材料,2009,40(2):246-249. |
| [8] | 张志萍,刘红飞,程晓农.化学共沉淀法合成低热膨胀ZrW2O8/ZrO2复合材料[J].复合材料学报,2008,25(4):138-142. |
| [9] | Sun L, Sneller A, Kwon P. ZrW2O8-containing composites with near-zero coefficient of thermal expansion fabricated by various methods. Comparison and optimization [J]. Compos Sci Technol, 2008, 68: 3425-3430. |
| [10] | Sun L, Kwon P. ZrW2O8/ZrO2 composites hy in situ synthesis of ZrO2--WO3: Processing, coefficient of thermal expansion, and theoretical model prediction [J]. Mater Sci Eng A, 2009, 527: 93-97. |
| [11] | 杨新波,程晓农,严学华,等.负热膨胀材料ZrW2O8及其复合材料研究进展[J].材料科学与工程学报,2007,25(1):160一163. |
| [12] | Evans J S O, Mary T A, Sleight A W. Negative thermal expansion in Se2 (WO4)3[J]. J Solid State Chem, 1998, 137 148-160. |
| [13] | Varga T, Wilkinson A P. Neutron powder diffraction study of the orthorhombic to monoclinic transition in SczW3O12 on compression [J].Solid State Sci, 2006, 8: 289-295. |
| [14] | Cetinkol M, Wilkinson A P, Chapman K W. Scandium tungstate above 2. 5 GPa [J]. Solid State Commun, 2008, 148: 511-515. |
| [15] | 朱君君,程晓农,杨娟.Sc2(WO4)3负热膨胀材料合成及其热性能[J].功能材料,2011,42(3):553-556. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%