应用铜模吸铸法制备出一系列的La62Al14-xMnxCu24 (x=1.0, 1.4, 2.0, 3.0, 4.0, 5.0)四元合金.通过Mn对Al的部分替代,研究了Mn元素微量替代对La62Al14Cu24三元块体非晶合金的玻璃形成能力和热力学稳定性的影响.实验结果表明,La-Al-Mn-Cu四元合金可以制备出直径达6 mm的完全非晶棒,说明了Mn对Al的部分替代能明显地增强La62Al14Cu24合金的玻璃形成能力.
参考文献
| [1] | Inoue A et al.[J].MRS Bulletin,2007,32:651-657. |
| [2] | Wang WH;Dong C;Shek CH .Bulk metallic glasses[J].Materials Science & Engineering, R. Reports: A Review Journal,2004(2/3):45-89. |
| [3] | Lou Q et al.[J].Journal of Non-Crystalline Solids,2009,355:759-775. |
| [4] | Zhang B et al.[J].Acta Materialia,2006,54:3025-3032. |
| [5] | Wang W H et al.[J].Progress in Materials Science,2007,52:540-596. |
| [6] | Li R et al.[J].Acta Materialia,2007,55:3719-3726. |
| [7] | Arata E R et al.[J].Acta Materialia,2008,56:651-658. |
| [8] | Jiang Q K et al.[J].Acta Materialia,2007,55:4409-4418. |
| [9] | Jiang Q K et al.[J].Journal of Alloys and Compounds,2006,424:183-186. |
| [10] | Zhang T et al.[J].Journal of Non-Crystalline Solids,1993,473:156-158. |
| [11] | Lu Z P et al.[J].Acta Materialia,2002,50:3501-3512. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%