研究Co-Al-W和商用MAN900合金在800 ℃ 75%Na2SO4+25%NaCl混合熔盐中的腐蚀动力学及热腐蚀行为.结果表明:7.5 W、9.8 W和10.7 W合金经热腐蚀后质量增加量比MAN900合金的质量增加量少,Co-Al-W合金的耐热腐蚀能力比MAN900合金的耐热腐蚀能力强.Co-Al-W合金在熔盐中腐蚀膜结构分成3层,即呈蓬松状由富钴氧化物Co3O4组成的腐蚀膜最外层,由Co、Al、W复杂氧化物组成的中间过渡层和主要由Al及Co氧化物组成较致密的腐蚀膜内层.随着腐蚀时间的增加,合金腐蚀膜最外层由于脱落逐渐变薄;中间过渡层厚度逐渐增加,该层中各元素分布趋于均匀、稳定;腐蚀膜内层致密性增加使该层增厚不明显.
参考文献
| [1] | 陈磊,王富岗.抗高温氧化合金的研究进展[J].材料导报,2002(05):27-29. |
| [2] | KAI W;LEE C H;LEE T W;WU C H .Sulfidation behavior of Inconel 738 superalloy at 500-900 ℃[J].Oxidation of Metals,2001,56(1/2):51-71. |
| [3] | MISRA R D K;SIVAKUMAR R .Effect of NaCl vapor on the oxidation of Ni-Cr alloy[J].Oxidation of Metals,1986,25(1/2):83-92. |
| [4] | ZHU Ri-zhang;GUO Man-jiu;ZUO Yu .Study of the mechanism of internal sulfidation-internal oxidation during hot corrosion of Ni-base alloys[J].Oxidation of Metals,1987,27(5/6):253-265. |
| [5] | BOURHIS Y;JOHN C S .Na2SO4 and NaCl-induced hot corrosion of six nickel-base superalloys[J].Oxidation of Metals,1975,9(06):507-528. |
| [6] | KAMESWA S R .The role of NaCl in the hot-corrosion behavior of nimonic alloy 90[J].Oxidation of Metals,1986,26(1/2):33-44. |
| [7] | CUI H;ZHANG J S;MURATA Y .Hot corrosion behavior of Ni-based superalloy with higher Cr contents.Part Ⅱ:Mechanism of hot corrosion behavior[J].Journal of University of Science and Technology Beijing Mineral Metallurgy Material,1996,3(02):91-98. |
| [8] | 黄乾尧;李汉康.高温合金[M].北京:冶金工业出版社,2000:100-133. |
| [9] | RAPP R I A .Hot corrosion of materials:A fluxing mechanism[J].Corrosion Science,2002,44(02):209-221. |
| [10] | 李云,郭建亭,袁超,杨洪才,徐宁,申志明.镍基铸造高温合金K35的热腐蚀行为[J].中国腐蚀与防护学报,2005(04):250-255. |
| [11] | Sato J;Omori T;Oikawa K;Ohnuma I;Kainuma R;Ishida K .Cobalt-base high-temperature alloys.[J].Science,2006(5770):90-91. |
| [12] | Akane Suzuki;Garret C. DeDolf;Tresa M. Pollock .Flow stress anomalies in gamma/gamma' two-phase Co-Al-W-base alloys[J].Scripta materialia,2007(5):385-388. |
| [13] | BELTRAN A M.Superalloys Ⅱ[M].New York:wiley,1987:135. |
| [14] | 李树索,韩雅芳,肖程波,宋尽霞.Ni3Al基合金IC6及MCrAlY包覆涂层的抗腐蚀性能[J].中国有色金属学报,2003(06):1451-1455. |
| [15] | ECER G M;MEIER G H .Oxidation of high-chromium Ni-Cr alloys[J].Oxidation of Metals,1979,13(02):119-158. |
| [16] | BEN-ABDERRAZIK G;MOULIN G;HUNTZ A M .Relation between impurities and oxide-scale growth mechanisms on Ni-34Cr and Ni-20Cr alloys.Ⅰ:Influence of C,Mn,and Si[J].Oxidation of Metals,1990,33(3/4):191-235. |
| [17] | 刘培生,陈国峰,梁开明.DZ40M钴基合金的高温氧化[J].中国腐蚀与防护学报,1999(06):339-344. |
| [18] | LUTHRA K L .Low temperature hot corrosion of cobalt-base alloys.part Ⅰ:Morphology of the reaction product[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1982,13:1843-1852. |
| [19] | 赵双群,谢锡善,Gaylord D.Smith.新型镍基高温合金在模拟燃煤锅炉环境中的腐蚀[J].金属学报,2004(06):659-663. |
| [20] | ZHANG J S;HU Z Q;MURATA Y;MORINAGA M,YUKAWA N .Design and development of hot-resistant nickel-base single crystal superalloys by the d-electrons alloy design theory.part Ⅱ:Effects of refractory metals Ti,Ta and Nb on microstructure and properties[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1993,24:2451-2463. |
| [21] | 李美栓.金属的高温腐蚀[M].北京:冶金工业出版社,2001:391-392. |
| [22] | 苏勇,孙长波,尹丽.Co及Co-10Ce合金在900℃空气中的热腐蚀行为研究[J].辽宁化工,2006(08):439-441. |
| [23] | 王淑荷;郭建廷;赖万慧;谭明辉 李辉 孙超 .NiAl-20%atFe合金的高温氧化与热腐蚀行为[J].中国腐蚀与防护学报,1995,15(02):135-140. |
| [24] | 赵双群,谢锡善.新型Ni-Cr-Co基高温合金的热腐蚀行为[J].材料科学与工艺,2006(05):506-509. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%