铝铅轴承合金带与具有不同厚度化合物层的热浸铝钢板通过热轧技术成功实现复合.复合界面结构分析表明:复合过程中形成两种界面,热浸铝钢板与铝铅合金带通过化合物界面结合与缺口界面结合的机制而复合.阐述了热浸时间、化合物层厚度、缺口界面分数之间的关系及对结合强度的影响,其中缺口界面分数是影响结合强度的主要因素.结合强度与缺口界面之间呈线性关系.缺口界面分数随化合物厚度的增加而增加,超过73μm,转为下降.
参考文献
| [1] | Pan D;Gao K;YU J .[J].Materials Science and Technology,1989,5:934. |
| [2] | Mohan S;Agarwala V;Ray S .[J].Wear,1990,140:83. |
| [3] | Mondolfo L F.Aluminum Alloys Structure and Propreties[M].London:Butterworth,1976:352. |
| [4] | Pathak J;Tiwari S N;Malhotra S L .[J].Wear,1986,112:341. |
| [5] | Mohan S;Agarwala V;Ray S .[J].Wear,1992,157:9. |
| [6] | Sharma A;Rajan T V .[J].Wear,1996,197:105. |
| [7] | 孙大仁;刘勇兵;安健.[J].中国有色金属学报,1998(zk):141. |
| [8] | Liu Yongbing;Sun Daren;An Jian.A New Cast Aluminum- lead Alloy for Automobile Industry[A].Beijing The Chinese Society for Metals,1997:355-358. |
| [9] | Adam G .[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1977,8A:973. |
| [10] | Gerhard L .[J].Practical Metallography,1977,14:251. |
| [11] | Eggeler G;Auer W;Kaesche H.[J].Journal of Materials Science,1986(02):3348. |
| [12] | EI- Mahallawy N A;Shady M A;EI- Sissi A R .[J].Materials Science and Technology,1997,13:832. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%