本文研究了LCB晶体主平面内有效非线性光学系数最大的相位匹配方向上的三倍频特性,所用LCB晶体切割方向为:θ=48.7°,φ=90°,晶体尺寸:4×4×10 mm3.测量了它的角度带宽:θ角的角度带宽△θ×1为1.15mrad-cm；φ角的角度带宽△φ×1为86.15 mrad-em.还对其温度带宽进行了测定,结果为7.6℃-cm.利用这块晶体,得到了最高为31.8％的三倍频转换效率,而在相同实验条件下用LBO晶体(尺寸与LCB相同)得到的转换效率最高为38.4％.
参考文献
| [1] | Wang C X;Wang G Y;Hicks A V et al.High-power Q-switched TEM00 Mode Diode Pumped Solid State Lasers with 》 30 W Output Power at 355 nm[J].Proceedings of Spie,2006,6100:6100191-61001914. |
| [2] | Wu Y C;Liu J G;Fu P Z et al.New Class of Nonlinear Optical Crystals R2 CaB10O19(RCB)[J].PROCEEDINGS OF THE SPIE,1998,3556:8-13. |
| [3] | Yicheng Wu;Jianguo Liu;Peizhen Fu;Junxing Wang;Huyun Zhou;Guofu Wang;Chuangtian Chen .A new lanthanum and calcium borate La_2CaB_(10)O_(19)[J].Chemistry of Materials,2001(3):753-755. |
| [4] | Fangli Jing;Peizhen Fu;Yicheng Wu;Yanlei Zu;Xian Wang .Growth and assessment of physical properties of a new nonlinear optical crystal: Lanthanum calcium borate[J].Optical materials,2008(12):1867-1872. |
| [5] | Zhang J X;Wang L R;Wu Y C et al.High-effiiciency Third Harmonic Generation at 355nm Based on La2CaB10O19[J].Optics Express,2011,19(18):16722-16729. |
| [6] | 万松明,傅佩珍,吴以成,王俊新,郑峰,官向国,周惠琼,陈创天.助熔剂法生长CaLa2B10O19晶体[J].人工晶体学报,2002(05):432-435. |
| [7] | 官向国,傅佩珍,万松明,周惠琼,吴以成,陈创天.CaLa2B10O19晶体生长及其定向[J].人工晶体学报,2002(04):333-336. |
| [8] | Yicheng Wu;Peizhen Fu;Feng Zheng;Songming Wan;Xiangguo Guan .Growth of a nonlinear optical crystal La_2CaB_(10)O_(19) (LCB)[J].Optical materials,2003(1/2):373-375. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%