WETTABILITY BETWEEN TiB_2 CERAMIC AND METALS

金属学报(英文版), 1999, 12(4): 395-400.

WETTABILITY BETWEEN TiB_2 CERAMIC AND METALS

J.Y. Zhang , Z.Y. Fu , W.M Wang , H. Wang and X.M. Min State Key Lab .of Advanced Technologyfor Materials Synthesis and Processing , Wuhan University of Technolo gy , Wuhan 430070 , China

Keywords： wetting , null , null

Self consistent Field discrete variational Xα( SCF Xα DV) method was used to study the wettabilitybetween TiB2 Ceramic and Metals. The Metals were Ni, Mo, Ni+ Mo, and etc. microstructureof TiB2/ Fe, TiB2/ Niand TiB2/ NiMoinvestigatedby TEM werechosen toidentify the calculation model. The result shows the wetting in the above systems were chemicalreactive wetting ,and can becalculated by SCF Xα DV . Theeffectof active ele ment( Mo) to TiB2/ Ni wettability wasstudied too.

参考文献

[1]

上一张下一张

PDF下载
导出引用
下载XML
收藏文章

计量

下载量()
访问量()

作者相关

在本站搜索
J.Y. Zhang Z.Y. Fu W.M Wang H. Wang and X.M. Min State Key Lab .of Advanced Technologyfor Materials Synthesis and Processing Wuhan University of Technolo gy Wuhan 430070 China
在百度学术搜索
J.Y. Zhang Z.Y. Fu W.M Wang H. Wang and X.M. Min State Key Lab .of Advanced Technologyfor Materials Synthesis and Processing Wuhan University of Technolo gy Wuhan 430070 China
在万方数据库搜索
J.Y. Zhang Z.Y. Fu W.M Wang H. Wang and X.M. Min State Key Lab .of Advanced Technologyfor Materials Synthesis and Processing Wuhan University of Technolo gy Wuhan 430070 China
在CNKI搜索
J.Y. Zhang Z.Y. Fu W.M Wang H. Wang and X.M. Min State Key Lab .of Advanced Technologyfor Materials Synthesis and Processing Wuhan University of Technolo gy Wuhan 430070 China

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网

WETTABILITY BETWEEN TiB_2 CERAMIC AND METALS

参考文献