The technology of plasma arc was used to modify the interface adhesion between chromium coating and steel substrate. The interface microstructure was studied as a function of plasma arc processing parameters. Microstructure analysis was performed by optical microscopy,scanning electron microscopy and electron probe. The microhardness distribution along the depth of a cross-section of the chromium coating and the substrate was measured. The results show the energy density of transferred plasma arc is obviously higher than plasma non-transferred arc. The molten interface was obtained by plasma transferred arc. Interfaces between chromium coating and steel substrate can be divided by plasma non-transferred arc into three classes: non-molten, a little molten and molten. Good interface bonding was obtained by proper process parameters. The microhardness of chromium coating decreases with increasing energy density of plasma arc.
参考文献
| [1] | Y.H.Tan;J.L.Doong.[J].WEAR,1991:43. |
| [2] | R.Wang;S.M.An;S.M.Wang.[J].Key Engineering Materials:279. |
| [3] | D Raghu;R Webber.[J].Welding:34. |
| [4] | L Bourithis;A Milonas;G D Papadimitriou.[J].Surface and Coatings Technology:286. |
| [5] | G F Liang.Manual of Cutting Technology[M].北京:机械工业出版社,1997:181. |
| [6] | Q K Cai;C S Liu;S Y Fu.[J].东南大学学报,1993:497. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%