对DD6单晶高温合金进行表面压痕处理,然后在不同温度(1220、1270和1310℃)热处理2h,研究合金再结晶的形核和长大行为.结果表明:γ'相溶解是再结晶的必要条件；再结晶晶粒以外,产生大量的亚晶界,离压痕中心越近,亚晶界密度越大,亚晶聚合粗化是再结晶的形核和长大机制.在γ'相溶解温度以上,γ'相对再结晶的形核和长大无明显影响.
参考文献
| [1] | Liu F.;Yang GC.;Guo XF. .Recrystallization mechanism for the grain refinement in undercooled DD3 single-crystal superalloy[J].Journal of Crystal Growth,2000(4):489-494. |
| [2] | Bond S D;Martin J W .Surface recrystallization in a single crystal nickel-based superalloy[J].Journal of Materials Science,1984,19(12):3867-3872. |
| [3] | Burgel R;Portella P D;Preuhs J.Recrystallization in single crystals of nickel base superalloys[A].,2000:229-238. |
| [4] | D. C. Cox;B. Roebuck;C. M. F. Rae .Recrystallisation of single crystal superalloy CMSX-4[J].Materials Science and Technology: MST: A publication of the Institute of Metals,2003(4):440-446. |
| [5] | Goldschmidt D;Paul U;Sahm P R.Porosity clusters and recrystallization in single-crystal components[A].,1992:155-164. |
| [6] | 曲彦平,刘丽荣,祖国庆,金涛,胡壮麒.DD6单高温合金热处理过程中的再结晶组织演化[J].材料工程,2011(08):14-18. |
| [7] | 熊继春;李嘉荣;刘世忠.单晶高温合金DD6表面再结晶组织[J].材料工程,2009(z1):110-113. |
| [8] | 刘丽荣 .一种镍基单晶高温合金的微观组织及蠕变性能的研究[D].沈阳:中国科学院金属研究所,2004. |
| [9] | Cahn R W.Physical Metallurgy[M].New York.:Elsevier Science BV,1996:2410-2416. |
| [10] | 胡庚祥;蔡珣.材料科学基础[M].上海:上海交通大学出版社,2000 |
| [11] | Bee J V;Jones A R;Howell P R .The interaction of recrystallization interfaces with intragranular precipitates dispersions in a nickel-base superalloy[J].Journal of Materials Science,1981,16:1471-1476. |
| [12] | 熊继春,李嘉荣,赵金乾,刘世忠,董建新.单晶高温合金DD6再结晶晶界析出相特征及其形成机制[J].金属学报,2009(10):1232-1236. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%