在单向压缩热模拟试验机上对AZ31-1Sm合金在变形温度为300～450℃、应变速率为0.01～1 s-1条件下的热变形行为和微观组织进行研究.结果表明:AZ31-1Sm镁合金在热压缩变形时,流变应力随着应变速率的增大和变形温度的降低而增大;该合金的热压缩流变应力行为可用双曲正弦形式的本构方程来描述,在本实验条件下,AZ31-1Sm镁合金热热变形激活能Q为160.8 kJ/mol.AZ31-1Sm易发生动态再结晶,在高变形温度和低应变速率条件下动态再结晶趋势明显,动态再结晶晶粒尺寸随着变形温度的增加和应变速率的降低而增大.
参考文献
| [1] | LI Jiqiang,DONG Xuanpu,FAN Zitian,WANG Yuanqing.Effects of Ce and Sb on the microstructure and properties of AZ91D magnesium alloy prepared by the EPC process[J].稀有金属(英文版),2008(01):41-45. |
| [2] | Zhang Guoying;Zhang Hui;Gao Ming .Mechanism of Effects of Rare Earths on Microstructure and Properties at Elevated Temperatures of AZ91 Magnesium Alloy[J].Journal of Rare Earths,2007(3):348-351. |
| [3] | McQueen HJ.;Ryan ND. .Constitutive analysis in hot working[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2002(1-2 Special Issue SI):43-63. |
| [4] | Dev, S;Stuart, AA;Kumaar, RCRD;Murty, BS;Rao, KP .Effect of scandium additions on microstructure and mechanical properties of Al-Zn-Mg alloy welds[J].Materials Science & Engineering. A, Structural Materials: Properties, Microstructure and Processing,2007(1-2):132-138. |
| [5] | Bardi F.;Cabibbo M.;Evangelista E.;Spigarelli S.;Vukcevic M. .An analysis of hot deformation of an Al-Cu-Mg alloy produced by powder metallurgy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2003(1/2):43-52. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%