通过溶胶凝胶法制备了Y、Gd共同掺杂的CeO2粉末(Ce0.8Y0.1 Gd0.1O1.9,CYG).并将制得的粉末经1400℃下高温烧结4h得到相应的CYG电解质烧结体.对CYG粉末及烧结体进行了相应的性能测试.实验结果表明:用溶胶凝胶法成功制备出了纳米CYG粉末,所得CYG粉末具有良好的烧结活性,1400℃下烧结所得电解质材料烧结体的相对密度达到95.8%.电导率的测试表明,CYG电解质烧结体在中温范围有较高的电导率,800℃时,其电导率达到了0.084S·cm-1.
参考文献
| [1] | 孟广耀,付清溪,彭定坤.中温固态氧化物燃料电池[J].太阳能学报,2002(03):378-382. |
| [2] | Zhu B .Advantage of intermediate temperature solid oxidefuel cells for traetionary applieations[J].Journal of Power Sources,2002,93:82-86. |
| [3] | 邱冠周,宋晓岚,曲鹏,杨振华,吴雪兰,王海波.影响纳米CeO2沉淀法合成的工艺因素研究[J].中国稀土学报,2005(03):321-327. |
| [4] | Matsui T;Minoru I;Mineshige A;Ogumi Z .Electrochemical properties of ceria-based oxides for use in intermediate-temperature SOFCs[J].Solid state ionics,2005(7/8):647-654. |
| [5] | Sha X Q;Lu Z;Huang X Q et al.Preparstion and properties of rare co-aoped Ce0.8 Sm0.2-x YxO1.9 electrolyte materials for SOFC[J].Journal of Alloys and Compounds,2006,424:315-321. |
| [6] | 杨乃涛,孟波,谭小耀.溶胶-凝胶法合成超细Ce1-xGdxO2-x/2电解质粉体[J].材料科学与工程学报,2004(04):572-575. |
| [7] | Wang F Y;Chen S Y;Wang Q et al.Study on Gd and Mg co-aoped ceria electrolyte for intermediate temperature solid oxide fule cells[J].Catalysis Today,2004,97:189-194. |
| [8] | 张立德;牟季美.纳米材料和纳米结构[M].北京:科学出版社,2001 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%