利用粉末冶金法制备了不锈钢多孔材料，研究了造孔剂含量对其孔隙率和抗压强度的影响。结果表明：随着造孔剂含量的增加，不锈钢多孔材料的平均孔隙率增大、抗压强度下降；造孔剂的质量分数控制在40％～50％之间时，可在保证强度的前提下使不锈钢多孔材料具有较高的孔隙卒。
Stainless steel porous materials were prepared by powder metallurgy method, and the effect of pore-forming material contents on the porosity and compressive strength was studied. The results show that the average porosity of the stainless steel porous materials increased and their compressive strength of the materials decreased with the increase of pore-forming material content. The mass fraction of pore-forming material being 40% --50% could make the strain[ess steel porous material owning high porosity.
参考文献
| [1] | 廖政,林建国,马蓦.钛镍多孔材料的制备及其显微组织与形状记忆性能[J].稀有金属材料与工程,2010(04):642-646. |
| [2] | 何俊升,冯小明.多孔陶瓷材料的制备技术与研究现状[J].铸造技术,2010(08):1101-1103. |
| [3] | 蔺绍江,熊惟皓,姚振华,瞿峻.烧结温度对316不锈钢粉末冶金烧结体组织和性能的影响[J].机械工程材料,2011(01):22-25. |
| [4] | 迟煜頔,汤慧萍,汪强兵,荆鹏,康新婷,葛渊.增塑挤压法制备不锈钢多孔过滤管[J].粉末冶金技术,2011(01):34-37. |
| [5] | 朱静,刘剑,杨屹.粉末冶金多孔不锈钢粉浆制备问题的研究[J].热加工工艺,2010(11):44-47,52. |
| [6] | 宋涛,熊旺,韩军.不锈钢过滤材料的过滤特性[J].原子能科学技术,2010(11):1397-1402. |
| [7] | 王乐,易健宏,戴煜,彭元东.压制压力对粉末冶金烧结硬化钢性能的影响[J].粉末冶金材料科学与工程,2008(02):97-101. |
| [8] | 贾宝强 .熔、溶脱盐造孔法制备金属通孔多孔材料研究[D].西安理工大学,2005. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%