研究了等通道转角挤压后时效处理对FeMnsiCrNiC合金碳化物的析出和形状记忆效应的影响.结果发现,挤压态合金经973 K时效处理150 min后,平均晶粒尺寸约10μm,同时晶内和晶界处析出大量碳化物.碳化物析出在回复完成前即开始,挤压产生的大量缺陷降低了碳化物析出的激活能,促进了碳化物析出.细晶强化和碳化物析出强化的共同作用显著提高了合金的基体强度,抑制预变形中的塑性变形,使更多的变形由应力诱发马氏体承担.因此,合金形状回复率达到89.4%(预变形4.33%时),比固溶态高120%,比直接时效高40%.
参考文献
| [1] | Otsuka H et al.[J].ISIJ International,1990,30:674. |
| [2] | 戎利建 et al.[J].金属学报,1995,31(03):125. |
| [3] | Chung C Y et al.[J].Mat Cha,1996,37:227. |
| [4] | Sato A;Maruyama T .[J].Scripta Materialia,2004,50:835. |
| [5] | Wen Y H;Yah M;Li N .[J].Sci Mat For,2000,327-328:223. |
| [6] | 董治中,刘文西,陈金铭,孙国光.NbC对FeMnSiCrNi合金组织与记忆性能的影响[J].稀有金属材料与工程,2003(11):927-929. |
| [7] | Segal V M .[J].Materials Science and Engineering,1995,A197:157. |
| [8] | Lin HK;Huang JC;Langdon TG .Relationship between texture and low temperature superplasticity in an extruded AZ31 Mg alloy processed by ECAP[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2005(1/2):250-257. |
| [9] | Iwahashi Y et al.[J].Scripta Materialia,1996,35:143. |
| [10] | Dutta B et al.[J].Acta Materialia,2001,49:785. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%