以介孔氧化钛晶须为载体,采用等体积浸渍法制备了Ni/TiO2催化剂,通过扫描电镜、X射线衍射、N2吸附脱附、热重分析和程序升温还原技术对催化剂及其前驱体进行了表征,考察了催化剂中Ni含量及焙烧和还原温度对催化剂催化对硝基苯酚加氢反应性能的影响.结果表明,Ni/TiO2催化剂不仅具有晶须状形貌和高结晶度的锐钛晶型,还保持了高比表面积和介孔结构.随着Ni/TiO2催化剂中镍负载量的增加,对硝基苯酚转化率逐渐增加,当镍负载量超过10%时,催化剂活性和选择性没有明显变化.当镍负载量为10%,焙烧和还原温度分别为500和450 ℃时,Ni/TiO2催化剂的加氢活性最佳,是Raney Ni的4倍.该催化剂循环使用7次后未发现明显失活.
参考文献
| [1] | 王延吉;王淑芳;高杨;赵新强 .[P].CN 200710151000.1,2007. |
| [2] | 徐南平;马振叶;张利雄;陈日志,刑卫红 .[P].CN 200710019458.1,2007. |
| [3] | Rode C V;Vaidya M J;Chaudhari R V .[P].US 6403833,2002. |
| [4] | Du Y;Chen HL;Chen RZ;Xu NP .Synthesis of p-aminophenol from p-nitrophenol over nano-sized nickel catalysts[J].Applied Catalysis, A. General: An International Journal Devoted to Catalytic Science and Its Applications,2004(1/2):259-264. |
| [5] | Vaidya M J;Kulkarni S M;Chaudhari R V .[J].Organic Process Research & Development,2003,7:202. |
| [6] | Yao H C;Emmett P H .[J].Journal of the American Chemical Society,1959,81:4125. |
| [7] | Vannice M A;Garten R L .[J].Journal of Catalysis,1979,56:236. |
| [8] | de Bokx P K;Bonne R L C;Geus J W .[J].Applied Catalysis,1987,30:33. |
| [9] | Vandeloosdrecht J.;Vandillen AJ.;Geus JW.;Vanderkraan AM. .METAL-SUPPORT INTERACTION - TITANIA-SUPPORTED AND SILICA-SUPPORTED NICKEL CATALYSTS[J].Journal of Catalysis,1997(2):217-226. |
| [10] | 熊峻,陈吉祥,张继炎.镍负载量对邻氯硝基苯加氢制邻氯苯胺Ni/TiO2催化剂性能的影响[J].催化学报,2006(07):579-584. |
| [11] | 尹红伟,陈吉祥,张继炎.焙烧及还原温度对对硝基苯酚加氢合成对氨基苯酚Ni/TiO2催化剂性能的影响[J].催化学报,2007(05):435-440. |
| [12] | 杨祝红,暴宁钟,刘畅,冯新,谢敬伟,吉晓燕,陆小华.TiO2纤维的制备及其光催化活性研究[J].高等学校化学学报,2002(07):1371-1374. |
| [13] | He M;Lu XH;Feng X;Yu L;Yang ZH .A simple approach to mesoporous fibrous titania from potassium dititanate[J].Chemical communications,2004(19):2202-2203. |
| [14] | 朱银华,周亚新,杨祝红,陆小华,冯新.新型Mo/TiO2的噻吩加氢脱硫性能[J].石油学报（石油加工）,2007(04):76-81. |
| [15] | Zhu Y H;Li W;Zhou Y X;Lu X H Feng X Yang Zh H .[J].Catalysis Letters,2009,127:406. |
| [16] | 刘金红,张倩,姚虎卿.Ni/AC催化剂的分散阈值及阈值效应[J].催化学报,2006(12):1139-1143. |
| [17] | 李建卫,黄星亮.低温选择性加氢镍催化剂的研究[J].石油化工,2001(09):673-676. |
| [18] | Kumbhar P S .[J].Applied Catalysis A:General,1993,96:241. |
| [19] | Ho SW.;Chen SG.;Chu CY. .Effect of thermal treatment on the nickel state and CO hydrogenation activity of titania-supported nickel catalysts[J].Journal of Catalysis,1998(1):34-48. |
| [20] | Rode C V;Arai M;Shirai M;Nishiyama Y .[J].Applied Catalysis A:General,1997,148:405. |
| [21] | 陈日志,杜艳,陈长林,邢卫红,徐南平,陈长祥,张正林.纳米镍与骨架镍催化性能比较[J].化工学报,2003(05):704-706. |
| [22] | Bradford M C J;Vannice M A .[J].Applied Catalysis A:General,1996,142:97. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%