采用99.999%分析纯的Al、Zn、Cu作原料,在外热式坩埚炉中熔制了5Cu40Zn55Al、15Cu20Zn65Al和3Cu17Zn80Al共3种合金,将其经过成分均匀化处理后,对包含亚稳相的3种合金分别进行球磨和手工锤击实验,采用X射线衍射仪分析合金平衡相组合.结果表明:合金通过球磨能得到窒温平衡相,而通过手工捶击则得不到室温平衡相;能否通过应力诱发相变快速获得室温合金平衡相组织与合金应力作用产生的变形机制有关;球磨能使合金内部发生大量变形,为合金向平衡相转变提供驱动力和原子扩散通道;而手工锤击主要是使合金发生以解理为主的脆性断裂,这种变形不能为亚稳相的转变提供必要的驱动力和原子扩散通道,从而得不到合金室温下的平衡相组成.
参考文献
| [1] | LEGENDRE B;FEUTELAIS Y;SAN JUAN J M;HURTADO I .Enthalpy of formation of the ternary T'phase in the Al-Cu-Zn system[J].Journal of Alloys and Compounds,2003,308(01):216-220. |
| [2] | LIANG H;CHANG Y A .A thermodynamic description for the Al2Zn2Cu system[J].Journal of Phase Equilibria,1998,19(01):25-37. |
| [3] | 陈辉,信昕,董丹阳,郝士明.Al-Zn-Cu系室温低Cu侧的相平衡关系[J].东北大学学报(自然科学版),2004(05):416-419. |
| [4] | 陈辉,信昕,任玉平,郝士明,李洪晓.Al-Zn-Cu系200℃低铜侧的相平衡[J].中国有色金属学报,2004(06):912-916. |
| [5] | 徐祖耀.应力对钢中贝氏体相变的影响[J].金属学报,2004(02):113-119. |
| [6] | 刘春成;姚可夫;高国峰;刘庄 .应力应变对马氏体相变动力学及相变塑性影响的研究[J].金属学报,1999,35(11):1125-1129. |
| [7] | 陆荣林,方如华.应力引起的镍钛单晶形状记忆合金相变的实验研究[J].力学季刊,2005(04):589-594. |
| [8] | Y. P. Ren;H. Ding;S. M. Hao .Abnormal refining of stepped-annealing microstructure in an Al alloy containing low copper and high zinc[J].Journal of Materials Science Letters,2003(6):433-436. |
| [9] | ZHU Y H .Milling induced microstructural change in furnace cooled eutectoid Zn-Al alloy[J].Journal of Materials Processing Technology,1997,63:624-627. |
| [10] | ZHU Y H .Structural evolution in mechanically milled eutectoid Zn-Al based alloy[J].Zeitschrift fur Metallkunde,1997,88:934-937. |
| [11] | QIAO Zhi-xia;LIU Yong-chang;WANG Dong-ai;NING Bao-qun LI Zong-min .Mechanism of stress induced γ→εmartensite transformation in an Fe2Mn2Si shape memory alloy[J].Journal of Materials Science and Engineering,2007,11:528-529. |
| [12] | 陈辉,罗继曼,韩泽光,许溪沙.Al-Zn-Cu系合金室温球磨中相变行为研究[J].沈阳建筑大学学报（自然科学版）,2007(04):672-675. |
| [13] | ZHU Y H;OROZCO E;TORRES J.Tensile creep deformation and microstructure change in cast Zn-Al alloy[J].Materials Transactions,1997(06):521-526. |
| [14] | ZHE Y H .Milling induced Zn-Al alloy[J].Journal of Materials Processing Technology,1997,63:624-630. |
| [15] | 陈玮,尹周澜,李晋峰.影响γ-Al2O3→α-Al2O3物相转变过程的因素研究[J].轻金属,2006(03):12-15. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%