研究了碳纳米管纤维的微观结构和拉伸性能,并进一步分析了其与环氧树脂形成界面剪切强度及微观结构.采用单丝断裂试验测试了碳纳米管纤维/环氧树脂复合材料体系的界面剪切强度,结合单丝断裂过程中的偏光显微镜照片、复合材料的拉曼谱图和断口扫描电镜照片,研究了碳纳米管纤维/环氧树脂复合材料界面的微观结构.结果表明:碳纳米管纤维/环氧树脂复合材料的界面剪切强度约为14 MPa;在碳纳米管纤维和环氧树脂形成界面的过程中,环氧树脂可以浸渍纤维,形成具有一定厚度的复合相,这种浸渍过程和界面相的形成都有利于碳纳米管纤维与基体之间的连接.
参考文献
[1] | Iijima S.Helical microtubules of graphitic carbon[J].Nature,1991354(6348):56. |
[2] | Lu W B;Zu M;Byun J H.State of the art of carbon nanotube fibers:opportunities and challenges[J].Advanced Materials,201224(14):1805-1833. |
[3] | Chou T W;Gao L M;Thostenson E T.An assessment of the science and technology of carbon nanotube-based fibers and composites[J].Composites Science and Technology,201070(01):1-19. |
[4] | 李珊;赵静娜;贾晶晶.阵列法制备连续碳纳米管纤维及其性能研究[J].玻璃钢/复合材料,2012(06):8-12. |
[5] | 孟凡成;周振平;李清文.碳纳米管纤维研究进展[J].材料导报,201024(09):38-43. |
[6] | Pham G T;Park Y B;Kramer L.Mechanical and electrical properties of polycarbonanotube buckypaper composite sheets[J].Nanotechnology,200819(32):325705. |
[7] | Gao Y;Li J Z;Liu L Q.Axial compression of hierarchically structured carbon nanotube fiber embedded in epoxy[J].Advanced Functional Materials,201020(21):3797-3803. |
[8] | Badaire S;Pichot V;Zakri C.Correlation of properties with preferred orientation in coagulated and stretch-aligned single-wall carbon nanotubes[J].Applied Physics,200496(12):7509-7513. |
[9] | Mora R J;Vilatela J J;Windle A H.Properties of composites of carbon nanotube fibres[J].Composites Science and Technology,200969(10):1558-1563. |
[10] | Hong S;Myung S.Nanotube electronics:A flexible approach to mobility[J].Nature Nanotechnology,20072(04):207. |
[11] | Deng F;Lu W;Zhao H.The properties of dry-spun carbon nanotube fibers and their interfaeial shear strength in an epoxy composite[J].Carbon,201149(05):1752-1757. |
[12] | Zu M;Li Q W;Zhu Y.The effective interfacial shear strength of carbon nanotube fibers in an epoxy matrix characterized by a microdroplet test[J].Carbon,201250(03):1271-1279. |
[13] | 张博明;孙新杨;李 嘉.电阻法在单丝碳纤维复合材料体系界面相传载能力评价中的应用[J].哈尔滨工程大学学报,201334(03):455-450. |
[14] | Chen T;Qiu L;Yang Z.An integrated energy wire for both photoelectric conversion and storage[J].Angewandte Chemie International Edition,201251(48):1977-1980. |
[15] | Chen T;Qiu L;Yang Z.Designing aligned inorganic nanotubes at the electrode interface:towards highly efficient photovoltaic wires[J].Advanced Materials,201224(34):4623-4628. |
[16] | 丘龙斌;孙雪梅;仰志斌.取向碳纳米管/高分子新型复合材料的制备及应用[J].化学学报,201270(14):1523-1532. |
[17] | Miao M H.Electrical conductivity of pure carbon nanotube yarns[J].Carbon,201149(12):3755-3761. |
[18] | Jia J J;Zhao J N;Xu G.A comparison of the mechanical properties of fibers spun from different carbon nanotubes[J].Carbon,201149(04):1333-1339. |
[19] | 蔡群;李敏;罗辑.单丝断裂能量法研究温度对碳纤维/环氧界面性能的影响[J].复合材料学报,201128(04):17-22. |
[20] | Risφ-R-1483(EN).Risφ-R-1483(EN) Testing procedure for the single fiber fragmentation test[S].Roskilde,Denmark:Risφ National Laboratory,2004. |
[21] | Wang Y;Zhang B M;Ye J R.Microstructures and toughening mechanisms of organoclay/polyethersulphone/epoxy hybrid nanocomposites[J].Materials Science and Engineering:A,2011528(27):7999-8005. |
[22] | 樊序敏;顾亦卓;刘亚男.碳纳米管浸润剂对碳纤维/环氧树脂界面性能的影响[J].复合材料学报,201229(04):17-22. |
[23] | Chipara D M;Macossay J;Ybarra A.Raman spectroscopy of polystyrene nanofibers-multiwalled carbon nanotubes composites[J].Applied Surface Science,2013275:23-27. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%