基于Gleeble-1500型热模拟试验机进行热压缩试验,通过对试验数据进行线性回归分析推导出了铸态42CrMo钢热压缩变形的本构方程,同时探讨了热压缩变形参数对显微组织的影响。结果表明：在相同的变形温度（850～1 150℃）下,该钢变形后的显微组织随着应变速率的增大逐渐变细,在5s-1时达到最细;在相同的应变速率（0.1～5s-1）下,显微组织随着变形温度的升高逐渐变细后再粗化,在1 050℃时马氏体板条最细;在相同的应变速率（1～5s-1）和变形温度（900～1 050℃）下,随着变形量的增加,再结晶晶粒尺寸均得到了显著细化;在温度为1 050℃、应变速率为5s-1、应变为0.6时热压缩后晶粒的细化效果最为显著。
Based on the thermal compression experiment on Gleeble-1500 thermal simulation machine,the constitutive equation of as-cast 42CrMo steel during hot compression deformation was derived through linear regression analysis for the test dadas.The effects of hot compression deformation parameters on microstructure were discussed.The results show that at the same deformation temperature（850-1 150 ℃）,the grains size of the steel after deformation decreased with the increase of the strain rate,and it reached the minimum at the strain rate of 5 s-1.At the same strain rate（0.1-5 s-1）,the microstructure decreased gradually,then increased with the increase of the deformation temperature,and the martensite lath reached the minimum at 1 050 ℃.The grains size decreased sighnificantly with the increase of the deformation at the same strain rate（1-5 s-1） and deformation temperature（900-1 050 ℃）.The best refining effect could be obtained after recrystallization could be obtained at temperature of 1 050 ℃,strain rate of 5 s-1 and strain of 0.6.
参考文献
| [1] | 蔺永诚,陈明松,钟掘.42CrMo钢形变奥氏体的静态再结晶[J].中南大学学报（自然科学版）,2009(02):411-416. |
| [2] | 林启权,张辉,彭大暑,林高用,王振球.热压缩2519铝合金流变应力特征[J].矿冶工程,2002(02):110-113. |
| [3] | 伍来智,陈军,张鸿冰.40Cr钢奥氏体动态再结晶及晶粒细化[J].上海交通大学学报,2008(05):786-790. |
| [4] | Sang-Hyun CHO;Ki-bong KANG;John J. JONAS .Mathematical Modeling of the Recrystallization Kinetics of Nb Microalloyed Steels[J].ISIJ International,2001(7):766-773. |
| [5] | 张斌 .结构钢热加工过程的物理与数值模拟[D].上海交通大学,2003. |
| [6] | 吴瑞恒,朱洪涛,张鸿冰,柳建韬,徐祖耀,阮雪榆.0.95C-18W-4Cr-1V高速钢动态再结晶的数学模型[J].上海交通大学学报,2001(03):339-342. |
| [7] | Dongsheng LIU;Alan O. HUMPHREYS;Mohammad R. TOROGHINEZHAD .The Deformation Microstructure and Recrystallization Behavior of Warm Rolled Steels[J].ISIJ International,2002(7):751-759. |
| [8] | 蔺永诚,陈明松,钟掘.42CrMo钢的热压缩流变应力行为[J].中南大学学报（自然科学版）,2008(03):549-553. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%