采用FeMo70合金和α-Al2O3粉体为原料,在1600 ℃保温2 h下埋炭无压烧结制备得到FeMo-Al2O3复相陶瓷.研究了FeMo70合金微粉的加入量对FeMo-Al2O3复相陶瓷的物相组成和力学性能的影响.结果表明,FeMo-Al2O3复相陶瓷中主要以α-Al2O3、Fe2Mo和Fe6Mo7N2三种物相形式存在.添加FeMo70合金后,Al2O3基体平均晶粒尺寸由4 μm增大到15 μm左右.FeMo-Al2O3复相陶瓷的洛氏硬度和断裂韧性均随FeMo70合金加入量的增加呈现出先增大后减小的趋势,且当FeMo70合金的加入量为13wt%时洛氏硬度(HRA)和断裂韧性(KIC)达到最大值,分别为88.3和3.7 MPa·m1/2.
参考文献
| [1] | Xinying Teng;Hanlian Liu;Chuanzhen Huang .Effect of Al_2O_3 particle size on the mechanical properties of alumina-based ceramics[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2007(1/2):545-551. |
| [2] | O. SBAIZERO;G. PEZZOTTI .INFLUENCE OF THE METAL PARTICLE SIZE ON TOUGHNESS OF Al_2O_3/Mo COMPOSITE[J].Acta materialia,2000(4):985-992. |
| [3] | O.Sbaizero;G.Pezzotti .Influence of residual and bridging stresses on the R- curve behavior of Mo- and FeAl-toughened alumina[J].Journal of the European Ceramic Society,2000(8):1145-1152. |
| [4] | E. Lucchini;S. Lo Casto;O. Sbaizero .The performance of molybdenum toughened alumina cutting tools in turning a particulate metal matrix composite[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2003(1/2):369-375. |
| [5] | Goffredo D P;Stefano G;Cesare M et al.Wear behaviour of Al2O3-Mo and Al2O3-Nb composites[J].Wear,2007,262:1346-1352. |
| [6] | M. Szafran;K. Konopka;E. Bobryk .Ceramic matrix composites with gradient concentration of metal particles[J].Journal of the European Ceramic Society,2007(2/3):651-654. |
| [7] | Aldridge M;Yeomans J A .The thermal shock behaviour of ductile particle toughened alumina composites[J].Journal of the European Ceramic Society,1998,19:1769-1775. |
| [8] | Lu J S;Gao L;Sun J et al.Effect of nickel content on the sintering behavior,mechanical and dielectric properties of Al2O3/Ni composites from coated powders[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2000,293:223-228. |
| [9] | Schicker S;Erny T;García D E et al.Microstructure and mechanical properties of Al-assisted sintered Fe/Al2O3 cermets[J].Journal of the European Ceramic Society,1999,19:2455-2463. |
| [10] | Konopka K;Ozieblo A .Microstructure and the fracture toughness of the Al2O3-Fe composites[J].Materials Characterization,2001,46:125-129. |
| [11] | K. Konopka;J.J. Bucki;S. Gierlotka .Characterization of the metal particles fraction in ceramic matrix composites fabricated under high pressure[J].Materials Characterization,2006(4/5):394-398. |
| [12] | Saucedo-Acuna RA;Monreal-Romero H;Martinez-Villafane A;Chacon-Nava JG;Arce-Colunga U;Gaona-Tiburcio C;De la Torre SD .High temperature oxidation-sulfidation behavior of Cr-Al2O3 and Nb-Al2O3 composites densified by spark plasma sintering[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2007(1-2):69-74. |
| [13] | Park N R;Lee D M;Ko I Y.Rapid consolidation of nanocrystalline Al2O3 reinforced Ni-Fe composite from mechanically alloyed powders by high frequency induction heated sintering[J].Ceramics International,2009 |
| [14] | Yang J Z;Huang Z H;Fang M H et al.Preparation and mechanical properties of Fe/Mo-Sialon composite ceramics[J].Scripta Materialia,2009,61:632-635. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%