通过溶胶-凝胶法合成了负载CaTiO3:Pr3+的多孔SiO2复合材料,并探究了材料的最佳煅烧温度.利用SEM、XRD、FT-IR研究了材料的结构,采用荧光分光光度计检测了材料的发光性能,为选择合适的温度提供了依 据.材料的激发波长为325nm和375nm;发射波长为613nm,对应于Pr3+的1D2-3 H4跃迁.随着煅烧温度由500℃升高到1000℃,发光强度先增大后减小,在800℃发光最强,且由SEM电镜看出,合成的材料分布均匀,呈球形,颗粒尺寸在500nm左右,煅烧之后材料的形貌及颗粒尺寸并未发生明显变化.
参考文献
| [1] | Li Guangzhi;Wang Zhenling;Yu Min et al.Fabrication and optical properties of core-shell structured spherical SiO2 @GdVO4:Eu3+ phosphors via sol-gel process[J].Journal of Solid State Chemistry,2006,179(08):2698. |
| [2] | Young Kyu Jeong;Hyug-Jong Kim;Hee Gyu Kim;Byung-Ho Choi.Luminescent properties of BaMgAl_(10)O_(17):Eu~(2+) blue phosphor grown with SiO_2 using atomic layer deposition[J].Current applied physics: the official journal of the Korean Physical Society,2009:S249-S251. |
| [3] | 刘建红,杨儒,刘家祥,李敏,严彩霞.有序介孔材料的合成及表征方法[J].材料导报,2002(09):52-55. |
| [4] | Chadha S S;Smith D W;Vecht A et al.New and improved phosphors for low-voltage applications[J].SID Digest,1994,51:1. |
| [5] | Diallo PT.;Mahiou R.;Cousseins JC.;Boutinaud P. .RED LUMINESCENCE IN PR3+-DOPED CALCIUM TITANATES[J].Physica Status Solidi, A. Applied Research,1997(1):255-263. |
| [6] | 李涛,沈明荣,袁小芳.柠檬酸为配位剂对Pr3+掺杂CaTiO3薄膜发光性能的影响[J].苏州大学学报（自然科学版）,2008(04):57-62. |
| [7] | Li Tao;Shen Mingrong;Fang Liang et al.Effect of Ca deficiencies on the photoluminescence of CaTiO3:Pr3+[J].Journal of Alloys and Compounds,2009,474(1-2):330. |
| [8] | 初本莉,刘行仁,王晓君,张家骅,蒋雪茵.偏硅酸钙中Pr3+的4f5d态的光谱特性及Pr3+→Gd3+的能量传递[J].光谱学与光谱分析,2002(04):542-544. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%