磷酸钙骨水泥(calcium phosphate cement,CPC)是一种常用的骨修复材料,并已应用于临床.但是,由于CPC自身的脆性较大和抗压强度不足,一般只能用于非负重区骨的修复.本文采用喷雾干燥法制备的生物可降解性聚乳酸纳米纤维来增强CPC,并对增强后的CPC的结构和性能进行了表征.结果表明,加入聚乳酸纳米纤维后,CPC的初凝时间缩短;固化后CPC的主晶相为羟基磷灰石;随着聚乳酸纳米纤维质量分数从0%增加到15%,CPC的平均湿态抗压强度从4.13±0.05MPa增加到8.71±O.10Mpa,湿态断裂韧性提高了约70%;当聚乳酸纳米纤维质量分数达20%时,抗压强度和断裂韧性都随之降低.断口分析和裂纹扩展实验结果表明,沿纤维能量耗散过程和纤维的桥联作用可能是性能增强的主要原因.
参考文献
| [1] | Miyamoto Y;Ishikawa K;Takechi M;Toh T;Yuasa T;Nagayama M;Suzuki K .Basic properties of calcium phosphate cement containing atelocollagen in its liquid or powder phases.[J].Biomaterials,1998(7/9):707-715. |
| [2] | Xu HH;Quinn JB .Calcium phosphate cement containing resorbable fibers for short-term reinforcement and macroporosity.[J].Biomaterials,2002(1):193-202. |
| [3] | Wang X;Ma J;Wang Y;He B .Structural characterization of phosphorylated chitosan and their applications as effective additives of calcium phosphate cements.[J].Biomaterials,2001(16):2247-2255. |
| [4] | 刘华 .骨诱导型可注射磷酸钙基骨修复材料的制备及性能研究[D].暨南大学,2007. |
| [5] | 沈卫,刘昌胜,顾燕芳.磷酸钙骨水泥的水化反应、凝结时间及抗压强度[J].硅酸盐学报,1998(02):129-135. |
| [6] | Liu CS;Shao HF;Chen FY;Zheng HY .Rheological properties of concentrated aqueous injectable calcium phosphate cement slurry[J].Biomaterials,2006(29):5003-5013. |
| [7] | 董浩,叶建东,王秀鹏,杨娟娟.磷酸钙骨水泥大孔径多孔组织工程支架的制备及其纤维增强[J].无机材料学报,2007(05):1007-1010. |
| [8] | 沈烈,乔飞,张宇强,张稚燕,彭懋,朱飞燕.炭纤维增强羟基磷灰石/聚乳酸复合生物材料的力学性能和体外降解性能[J].复合材料学报,2007(05):61-65. |
| [9] | 戴红莲,李世普,贺建华,闫玉华.碳纤维增强alpha-TCP/TTCP骨水泥的研究[J].无机材料学报,2004(05):1025-1030. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%