研究了变形钽丝在不同温度下退火后的织构演变和再结晶行为,发现1360℃退火后钽丝初次再结晶基本完成;1500℃退火后,钽丝中发生了二次再结晶,晶粒异常粗大.提出了拉拔钽丝的再结晶织构模型.
参考文献
| [1] | Briant C.L.;MacDonald E. .Recrystallization textures in tantalum sheet and wire[J].International Journal of Refractory Metals & Hard Materials,2000(1):1-8. |
| [2] | Feng C;Kumar P.Correlating microstructure and texture in cold-rolled Ta ingot[J].Journal of Metals,1989:40. |
| [3] | 张新明,张少睿,周卓平,舒永春.钽丝的拉拔及退火织构[J].中国有色金属学报,1999(04):774-778. |
| [4] | 程肃之;花礼先;阚希文.液体钽电容器阳极引出线用钽丝表面质量定量检验方法[J].物理测试,1990(04):39. |
| [5] | 毛卫民;赵新兵.金属的再结晶与晶粒长大[M].北京:冶金工业出版社,1994:29. |
| [6] | Bunge H J.Texture Analysis in Materials Science[M].London:Butterworths,1982:47. |
| [7] | Bevis Hutchinson .Nuleation of recrystallization[J].Scripta Metallurgica et Materialia,1992,27:1471. |
| [8] | Park YB.;Gottstein G.;Lee DN. .A model of the development of recrystallization textures in body centered cubic metals[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,1998(1):178-184. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%