为了探究管线钢L360Q在CO2体系气田采出水中的腐蚀行为,采用电化学法、失重法、扫描电镜及能谱分析技术,针对国内某气田腐蚀环境,研究了气田模拟采出水中温度、腐蚀时间、腐蚀介质流态对L360Q腐蚀的影响.结果表明:温度升高导致L360Q开路电位负移,阻抗值减小;而随着腐蚀时间的延长,开路电位正移,阻抗值增大.温度的升高加速了L360Q的腐蚀;随着腐蚀时间的延长,L360Q腐蚀速率下降,L360Q在模拟气田水中的腐蚀产物主要为FeCO3.腐蚀介质的流动能够提高L360Q的腐蚀速率.
参考文献
| [1] | 黄雪松;安思彤;陈长风.普光气田集输管材腐蚀评价及缓蚀剂加药工艺优化[J].天然气工业,2011(9):120-123. |
| [2] | M. Honarvar Nazari;S.R. Allahkaram;M.B. Kermani.The effects of temperature and pH on the characteristics of corrosion product in CO_2 corrosion of grade X70 steel[J].Materials & design,20107(7):p.3559. |
| [3] | S. L. Wu;Z. D. Cui;F. He.Characterization of the surface film formed from carbon dioxide corrosion on N80 steel[J].Materials Letters,20046(6):1076-1081. |
| [4] | 姜放;戴海黔;曹小燕;黄红兵.油套管在CO2和H2S共存时的腐蚀机理研究[J].石油与天然气化工,2005(3):213-215. |
| [5] | 王晓博;俞宏英;关望;孙冬柏.X52钢在普光气田服役条件下的CO2腐蚀行为[J].材料工程,2014(8):72-78. |
| [6] | E. Machnikova;Kenton H. Whitmire;N. Hackerman.Corrosion inhibition of carbon steel in hydrochloric acid by furan derivatives[J].Electrochimica Acta,200820(20):6024-6032. |
| [7] | W.Meuleman;R.Vandenkerckhove.Electrochemical investigation of automotive coating system[J].Materials Science Forum,1998Pt.1(Pt.1):383-396. |
| [8] | P.Campestrini;E.P.M.van Westing;J.H.W.de Wit.Influence of surface preparation on performance of chromate conversion coatings on Alclad 2024 aluminium alloy Part I: Nucleation and growth[J].Electrochimica Acta,200116(16):2553-2571. |
| [9] | 郑俊涛;潘莹;郑鹏华;张三平.903钢在NaC1溶液和薄液膜中的腐蚀规律[J].材料保护,2010(3):27-29. |
| [10] | 赵国仙;陈长风;李建平;魏云峰;沈建新;路民旭.X52钢的CO2腐蚀行为[J].腐蚀科学与防护技术,2001(4):236-238. |
| [11] | 万里平;孟英峰;梁发书.油气田开发中的二氧化碳腐蚀及影响因素[J].全面腐蚀控制,2003(2):14-17. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%