STUDY ON FATIGUE DAMAGE BELOW THE FATIGUE LIMIT AND THE COAXING EFFECTS

金属学报(英文版), 1996, 9(3): 227-231.

STUDY ON FATIGUE DAMAGE BELOW THE FATIGUE LIMIT AND THE COAXING EFFECTS

WU Zhixue , LU Wenge and XU Hao1)(Fushun Petroleum institute , Fushun 113001 , China)2)(State Key Laboratory for Fatigue and Fracture of Materials , Institute of Metal Research , ChineseAcademy of Sciences , Shenyang 110015 , China)3)(Institute of Mechanical Engineering , Northeastern University , Shenyang 110006 , China)Manuscript received 19 July 1995 , in revised form 11 April 1996

Keywords： : fatigue damage , null , null

Rotary bending fatigue tests were carried out for smooth specimens of a mediumcarbon steel with two different grain sizes near the fatigue limit. The process of fatigue damagewas observed by replication method, and the effects of grain size,stress level and microstructure on surface damage were studied. The effect of following cycle stress level on the coaxing effects was also discussed. The fatigue limit is the maximum stress at which the short fatigue crack initiates and becomes a non-propagating crack.. The length of non-propagating crack is related to grain sizes and stress level. The coaxing effects disappear when the following stress level is greater than the critical value.

参考文献

[1]

上一张下一张

计量

下载量()
访问量()

作者相关

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网

STUDY ON FATIGUE DAMAGE BELOW THE FATIGUE LIMIT AND THE COAXING EFFECTS

参考文献