以富含硼、镁、锂的盐湖卤水为原料,采用硫酸和离子交换法联合提硼,实现硼与镁、锂分离;采用氨法沉淀镁实现镁与锂的分离.分别用静态法和动态法研究卤水pH值、吸附温度、吸附时间、树脂用量、卤水流速、交换柱高径比对硼提取率的影响,确定提硼最佳工艺条件,硼提取率达95%以上.研究卤水硼浓度对氢氧化镁中硼含量的影响.结果表明:当卤水中的硼浓度由4.54 mg/L增加到1200 mg/L时,氢氧化镁中硼含量由0.04 mg/g增加到8.82 mg/g.对硼浓度4.54 mg/L的卤水用氨法沉淀制备氢氧化镁,在1500℃下煅烧得到氧化镁,其纯度为99.8%.
@@@@Using salt lake brine with high boron, magnesium and lithium as raw material, the boron was separated from magnesium and lithium with sulfate acid and ion exchange resin, and the magnesium was separated by precipitation with ammonia. The effects of pH value, temperature, time, resin amount, flowing rate of brine and ratio of height to diameter (H/D) of the column on boron removal were investigated under static and dynamic conditions. The optimum process conditions of boron removal are obtained. The results show that the boron removal ratio reaches 95%under the optimum process conditions. The boron concentration of brine has a significant effect on the content of boron in magnesium hydroxide. The content of boron in magnesium hydroxide increases from 0.04 mg/g to 8.82 mg/L with boron increasing from 4.54 mg/L to 1 200 mg/L. Using brine containing 4.54 mg/L boron as raw material to prepare magnesium hydroxide followed by calcination at 1 500℃for 2 h, 99.8%magnesium oxide is obtained.
参考文献
| [1] | 李浩,唐中凡,刘传福,雷光元.新疆罗布泊盐湖卤水资源综合开发研究[J].地球学报,2008(04):517-524. |
| [2] | 许荣辉,李海民.高纯氧化镁制备原理初探[J].盐湖研究,2003(04):39-41. |
| [3] | 杨建元;程温莹;邓天龙;高晶岩.东台吉乃尔湖晶间卤水综合利用研究(煅烧法提锂工艺)[J].无机盐工业,1996(02):29-33. |
| [4] | 张占良,索智录.盐湖卤水煅烧制取含锂氧化镁的实验研究[J].内蒙古石油化工,2008(18):19-20. |
| [5] | Xianming Wen;Peihua Ma;Chaoliang Zhu;Qiong He;Xiaochuan Deng .Preliminary study on recovering lithium chloride from lithium-containing waters by nanofiltration[J].Separation and Purification Technology,2006(3):230-236. |
| [6] | 宋卫得,王海增,邢坤,郭鲁钢,李冬梅.纳滤膜分离技术及其在盐湖卤水资源开发中的应用[J].盐湖研究,2006(04):56-60. |
| [7] | NADAV N .Boron removal from seawater reverse osmosis permeate utilizing selective ion exchange resin[J].DESALINATION,1999,124:131-135. |
| [8] | Cyril Jacob .Seawater desalination:Boron removal by ion exchange technology[J].Desalination: The International Journal on the Science and Technology of Desalting and Water Purification,2007(1/3):47-52. |
| [9] | 徐徽,许良,陈白珍,石西昌,杨鑫.高镁锂比盐湖卤水镁锂分离工艺[J].中南大学学报（自然科学版）,2009(01):36-40. |
| [10] | 杨鑫,徐徽,陈白珍,石西昌,许良.盐湖卤水硫酸法提取硼酸的工艺研究[J].湖南师范大学自然科学学报,2008(01):72-77. |
| [11] | 王路明.Mg（OH）2对海水中硼的吸附效果[J].海湖盐与化工,2003(05):5-7. |
| [12] | 杨卉破,李琦,王秋霞,余丽秀,曹耀华.从卤水中回收硼的试验研究[J].矿产保护与利用,2002(04):39-42. |
| [13] | Nuri Unlu;Mustafa Ersoz .Removal of heavy metal ions by using dithiocarbamated-sporopollenin[J].Separation and Purification Technology,2007(3):461-469. |
| [14] | Naiya TK;Bhattacharya AK;Das SK .Removal of Cd(II) from aqueous solutions using clarified sludge[J].Journal of Colloid and Interface Science,2008(1):48-56. |
| [15] | H.Koseoglu;N.Kabay;M.Yiiksel .The removal of boron from model solutions and seawater using reverse osmosis membranes[J].Desalination: The International Journal on the Science and Technology of Desalting and Water Purification,2008(1/3):126-133. |
| [16] | EDWARDS J O;ROSS V J .Structural principles of the hydrated polyborates[J].Journal of Inorganic and Nuclear Chemistry,1960,15(04):329-337. |
| [17] | Robert H. Byrne;Wensheng Yao;Kateryna Klochko;John A. Tossell;Alan J. Kaufman .Experimental evaluation of the isotopic exchange equilibrium ~(10)B(OH)_3 + ~(11)B(OH)_4~- = ~(11)B(OH)_3 + ~(10)B(OH)_4~- in aqueous solution[J].Deep-sea research, Part II. Topical studies in oceanography,2006(4):684-688. |
| [18] | 肖应凯,肖云,G.H.Swihart,刘卫国.硼特效性树脂离子交换法分离硼的研究[J].盐湖研究,1997(02):1. |
| [19] | 孔亚杰,李海民,韩丽娟.D403树脂从盐湖卤水中提取硼酸的探索试验[J].无机盐工业,2006(07):42-43. |
| [20] | 许良 .盐湖卤水镁锂分离及制取碳酸锂工艺研究[D].中南大学,2008. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%